Polymer Property : Flexural Modulus = 899 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	6.20 GPa	899 ksi
Plastcom SLOVALEN PH 69 GF 45 PP, 45% glass fibre FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 45% glass fibre, contains the modifier of mechanical properties.Thermo stable. Increased strength in comparison wit..
Flexural Modulus	6.20 GPa	899 ksi
Plastcom SLOVAMID 6 NG1 GF 20 HLS PA6, 20% glass fibre, combined stability FeaturesPA 6 for injection moulding, chemically strengthened with 20% glass fibre, heat and wheather stabilized. Stabilized against hydrolisys. Good surface finisch. Scratch resistent.Packaging, tra..
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, Dry As Molded AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent cre..
Flexural Modulus	6.20 GPa	899 ksi	2mm/min; ASTM D790
Kingfa JH710 G20 Flame Retardant & 20% Glass Fiber Reinforced PC Features:Environmental friendly flame retardantUL V-0 @ 1.6mmHigh mechanical strengthGood size stability, good surfaceSuitable for exact moldingApplications:CD-ROM, DVDPrinter, photocopier cabinetSc..
Flexural Modulus	6.20 GPa	899 ksi	Tangent at 0.05 in/min; ASTM D790A
LyondellBasell Higlass PF072-3 Polypropylene Homopolymer, 30% Glass Fiber Key Features: conventional melt flow, high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, high rigidity, high strength, good impact resistanceApplications: appliance ..
Flexural Modulus	6.20 GPa	899 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC LNP* Lubricomp* Lexan_LF1520A compound is a 20% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
Flexural Modulus	6.20 GPa	899 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP QFP36 PA6.10 (Europe-Africa-Middle East) LNP* LUBRICOMP* QFP36 is a compound based on PA6.10 resin containg Glass Fiber, PTFE, Silicone. Added features include: Internally Lubricated.
Flexural Modulus	6.20 GPa	899 ksi	ISO 178
Solvay TECHNYLSTARâ„¢ S 216 V35 PA6, 35% glass filled, Conditioned Description: TECHNYLSTAR polyamide, reinforced with 35% of glass fiber, for injection molding. Characterized by a high fluidity of the melt.Available in: Europe and North AmericaProduct Applications..
Flexural Modulus	6.20 GPa	899 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics ValoxÂ® SHF434HR PBT PBT, Super High Flow, 20% glass reinforced,hydrolytically resistant.
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP DF0049E PC (Asia Pacific) LNP* Thermocomp* DF0049E is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Easy Molding, Flame Retardant.
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP GF004 PSU LNP* Thermocomp* GF004 is a compound based on Polysulfone resin containing 20% Glass Fiber.
Flexural Modulus	6.20 GPa	899 ksi	ASTM D 790
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly (Asia Pacific) LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Modulus	6.20 GPa	899 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP MF006A PP (Europe-Africa-Middle East) LNP* THERMOCOMP* MF006A is a compound based on Polypropylene resin containing Glass Fiber.
Flexural Modulus	6.20 GPa	899 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP THERMOCOMP MF006AS PP LNP THERMOCOMP* MF006AS is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized.
Flexural Modulus	6.20 GPa	899 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics NORYL GTX GTX830 PPE+PA (Europe-Africa-Middle East) NORYL GTX830 a 30% glass reinforced grade which offers an excellent combination of chemical/heat resistance in combination with stiffness.
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP MF006SXP PP LNP THERMOCOMP* MF006SXP is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Chemically Coupled.
Flexural Modulus	6.20 GPa @Thickness 4.00 mm	899 ksi @Thickness 0.157 in	2mm/min, injection molded, unannealed; ISO 178
Styron EMERGEâ„¢ 5302 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5302 is a black, 20% glass-filled ABS which is suitable for use in a wide variety of internal structural component applications in the information technology market. Applications: ..
Flexural Modulus	6.20 GPa	899 ksi	2mm/min; ISO 178
Borealis GB311U Polypropylene Compound, Glass Fiber Reinforced GB311U is a 30% chemically coupled glass fiber reinforced polypropylene compound intended for injection molding. This material shows excellent mechanical properties also at elevated temperatures. ..
Flexural Modulus	6.20 GPa	899 ksi	DIN 52457
CP-Polymer-Technik Wellamid® 6600 MF30 HWCP 30% Milled Glass Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Flexural Modulus	6.20 GPa	899 ksi	ISO 178
DuPont Performance Polymers Crastin® SK603 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**) 20% Glass Reinforced Polybutylene Terephthalate Crastin SK603 NC010 is a 20% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont P..
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
Ashley Polymers Ashlene® 527-33G Nylon 66, 33% Glass Reinforced A 33% glass reinforced impact modified Nylon 66.Data provided by the manufacturer
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
A. Schulman ComAlloy Comtuf® 105 Polypropylene, Glass Reinforced, Chemically Coupled, Impact Modified Data provided by the manufacturer, ComAlloy International Company.40% Glass Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been int..
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
A. Schulman ComAlloy Voloy® 631 Nylon 6/6, Glass Reinforced, Flow Enhanced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.13% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Flexural Modulus	6.20 GPa	899 ksi	dry; ISO 178
Azoty Tarnow™ Tarnamid® T-27 GF20 GB10 Polyamide 6 - Glass Beads Reinforced 20% Glass fiber and 10% glass beads reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following ..
Flexural Modulus	6.20 GPa	899 ksi	ASTM Data
BASF Capron® 8334G Impact Modified, 40% Glass-Filled Nylon 6 (Conditioned) (discontinued **) Capron 8334G is a heat stabilized, 40% glass fiber reinforced polyamide 6 molding compound developed for applications requiring a high level of stiffness combined with excellent impact performance. ..
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Asia Pacific) LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Internally Lubricated.
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
Plenco 7321 Phenolic, Nodular, Injection Molded PLENCO 07321 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and excellent dimensional stability. Type ASTM 5948 CFI-5, and UL recognized under compon..
Flexural Modulus	6.20 GPa	899 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Internally Lubricated.
Flexural Modulus	6.20 GPa	899 ksi	ASTM-D790
Polyram RamOfin PPH308G8 Polypropylene, 40% Glass Fiber 40% glass fiber reinforced, heat stabilized, impact modified polypropylene for injection molding applicationsInformation provided by Polyram Ram On Ind.