Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPS7R PC Low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam, e-beam, and gamma sterilizable. .. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® OQ3820 PC (Europe-Africa-Middle East) High Viscosity, UV-stabilized grade for ophthalmic lenses. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® SLX1432 PC Copolymer Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. Available in opaque colors. Typical minimum color tolerance limit is DE CMC < 1.0 |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® SLX1432T PC Copolymer (Asia Pacific) Medium viscosity PC copolymer with enhanced UV stabilization and added release agent. Available in transparent and tinted colors. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SLX1482T PC Copolymer Medium viscosity PC Copolymer, enhanced UV stabilization. Transprarent and tinted colors. Higher mold release content than SLX1432T.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527 |
Nilit FRIANYL A63 AV15 Nylon 6.6 for injection molding Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC LNP* Lubricomp* Lexan_LF1510A compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC (Europe-Africa-Middle East) LNP* Lubricomp* Lexan_FL1510 compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® 4012G PBT VALOX 4012G is a 10% glass fiber reinforced PBT injection molding resin with excellent mechanical properties. Applications: connectors. This grade is a 4012 with improved cycle time and ductility. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics Valox® 771 PBT 35% mineral/glass reinforced flame retardant grade with a CTI performance level class of 0 rating. Applications which may see electrical arcing. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU (Asia Pacific) LNP* Thermocomp* GX05482 is a compound based on Polysulfone resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
Styron CALIBRE™ 2060-6 Polycarbonate Resin Overview: CALIBRE™ 2060-6 polycarbonate resin is used in medical applications involving steam or ethylene oxide sterilization – through suitability for use in these applications is depende.. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
Styron CALIBREâ„¢ 301-6 Polycarbonate Resin Overview: CALIBREâ„¢ 300-6 polycarbonate resins offer exceptional impact resistance, heat distortion resistance and optical clarity as well as high melt strength for blow molding and sheet applic.. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
Styron CALIBREâ„¢ 301V-6 Polycarbonate Resin Overview: CALIBREâ„¢ 301V-6 Polycarbonate resins offer exceptional impact resistance and heat distortion resistance, and meets UL94 V-2 rating. CALIBRE 301V-6 contains a mold release agent and is.. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp RX06324 PA 66 (Asia Pacific) This material is Mineral filled Nylon grade with high dielectric constantThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-2/50 |
Styron CALIBREâ„¢ 300-6 Polycarbonate Resin Overview: CALIBREâ„¢ 300-6 polycarbonate resin offer exceptional impact resistance, heat distortion resistance, and optical clarity as high melt strength for blow molding and sheet applications. .. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-93 |
Wellman EcoLon® MR1660-BK 40% Mineral Reinforced Post Consumer Compound Nylon 66 Description: Mineral Reinforced Post Consumer Compound Nylon 66Information provided by Wellman. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 73G15L NC010 Nylon 6
(Unverified Data**) 15% Glass Reinforced Polyamide 6Zytel 73G15L NC010 is a 15% glass fiber reinforced polyamide 6 resin for injection molding.Information provided by DuPont Performance Polymers |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527 |
Eurotec® Tecolen® HP30 KG30 NL HS 0B PPCP, 30% glass fiber/glass bead reinforced, heat stabilized, natural Information provided by Eurotec® |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527 |
Cossa Polimeri ESTABLEND PA 1050 GF HI ABS / Nylon 6 Blend, 25% Glass Filled ESTABLEND PA is a blend of acrylonitrile butadiene styrene and polyamide 6.25% glass fiber reinforcedHigh impact strength, high chemical resistance, excellent heat resistance, high dimensional stabi.. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527-1/-2 |
DSM Akulon® S223-G2U (Cond.) 13% Glass Reinforced Nylon 66 (North America) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO R 527 |
Addiplast Addinyl A2H M30 Flame Retardant Nylon 66, 30% Mineral Filled Flame retardant, 30% mineral filled, with halogensInformation provided by Addiplast. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | 50%RH; ISO 527-1/-2 |
DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66
(Unverified Data**) 14% Glass Reinforced Toughened Heat Stabilized Polyamide 66 Zytel 80G14AHS NC010 is a 14% glass fiber reinforced toughened high flow heat stabilized polyamide 66 resin. It offers outstanding perform.. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | ISO 527 - 1 & - 2 |
Asahi Kasei Tenac® SH410 Homopolymer Acetal Resin General purpose grade, high impact, high elongation, medium viscosityInformation provided by Asahi Kasei Corporation. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® SLX1482T PC Copolymer (Europe-Africa-Middle East) Medium viscosity PC Copolymer, enhanced UV stabilization. Transprarent and tinted colors. Higher mold release content than SLX1432T.This data was supplied by SABIC-IP for the Europe-Africa-Middle E.. |
|||
Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Thermocomp TX88477 PU LNP* Thermocomp* TX88447 is a compound based on Polyurethane resin containing proprietary fillers.This data was supplied by SABIC-IP for the Americas region. |