Polymer Property : Linear Mold Shrinkage, Transverse = 0.0035 in/in Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Linear Mold Shrinkage, Transverse	0.0035 - 0.0060 cm/cm @Thickness 3.17 mm	0.0035 - 0.0060 in/in @Thickness 0.125 in
Ovation Polymers Nima™ NH PA66UT Nylon 66 Polyamide 66 - Ultra Tough, Flame Retarded Non-Hal grade with excellent retention of mechanical properties. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humi..
Linear Mold Shrinkage, Transverse	0.0035 cm/cm @Time 86400 sec	0.0035 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS (Asia Pacific) LNP* Faradex* NS003 is a compound based on PC+ABS Blend resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
Linear Mold Shrinkage, Transverse	0.0035 cm/cm @Time 86400 sec	0.0035 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP FARADEX NS003 PC+ABS (Europe-Africa-Middle East) LNP* Faradex* NS003 is a compound based on PC+ABS Blend resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in	LATI
LATI LARIL 13-V1KC Mineral Filled Polyphenylene Oxide (PPOm) (UL94V-1) (Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most ..
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in
Ineos ABS TriaxÂ® 1315 GF ABS + Polyamide Blend (Conditioned) Key Features:Contains FillerSuitable processing methods:Injection molding
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in
Ineos ABS TriaxÂ® 1315 GF ABS + Polyamide Blend (DAM) Key Features:Contains FillerSuitable processing methods:Injection molding
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in	ISO 294-4, 2577
Lanxess DurethanÂ® DP 2037/30 H2.0 LT 904040 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, black colored for laser transmission-welding (laser-transparent), good heat-ageing resistance
Linear Mold Shrinkage, Transverse	0.0035 - 0.0055 cm/cm	0.0035 - 0.0055 in/in
LATI Latamid 66 H2 K/50 PA 66, 50% Carbon Fiber Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termopl..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0060 cm/cm	0.0035 - 0.0060 in/in
LATI KelonÂ® B FR H CET/30-V0 PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Low thermal expansion coefficient. Very high dimensional stab..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0060 cm/cm	0.0035 - 0.0060 in/in
LATI Larpeek 10 K/20 PEEK, 20% Carbon Fiber Reinforced Polyetheretherketone (PEEK) based compound. Carbon fiber. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; As..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0055 cm/cm	0.0035 - 0.0055 in/in
LATI Latiohm 87/28-05 PD01 G/10 PC, 10% Glass Fiber Reinforced Semiconductive/dissipative product based on Polycarbonate (PC). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0050 cm/cm	0.0035 - 0.0050 in/in
LATI Latiohm 90/13-09 PD01 G/10 PPOm, 10% Glass Fiber Reinforced Semiconductive/dissipative product based on Modified Polyphenylene Oxide (PPOm). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation prov..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0050 cm/cm @Thickness 3.20 mm	0.0035 - 0.0050 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC LNP* Lubricomp* Lexan_LF1510A compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
Linear Mold Shrinkage, Transverse	0.0035 - 0.0050 cm/cm @Thickness 3.20 mm	0.0035 - 0.0050 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC (Asia Pacific) 10% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
Linear Mold Shrinkage, Transverse	0.0035 - 0.0050 cm/cm @Thickness 3.20 mm	0.0035 - 0.0050 in/in @Thickness 0.126 in	SABIC Method
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC (Europe-Africa-Middle East) LNP* Lubricomp* Lexan_FL1510 compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
Linear Mold Shrinkage, Transverse	0.0035 - 0.0040 cm/cm @Time 86400 sec	0.0035 - 0.0040 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP LUBRICOMP OCL36XXP PPS - Linear (Europe-Africa-Middle East) LNP* LUBRICOMP* OCL36XXP is a compound based on PPS- Linear resin containing PTFE, Carbon Fiber. Added features include : Internally Lubricated, Electrically Conductive .
Linear Mold Shrinkage, Transverse	0.0035 cm/cm @Time 86400 sec	0.0035 in/in @Time 24.0 hour	ASTM D 955
SABIC Innovative Plastics LNP Thermocomp DF0066P PC LNP THERMOCOMP* DF0066P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing.This data was supplied by..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0040 cm/cm	0.0035 - 0.0040 in/in	ISO 294-4
Styron EMERGEâ„¢ 5302 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5302 is a black, 20% glass-filled ABS which is suitable for use in a wide variety of internal structural component applications in the information technology market. Applications: ..
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in	ISO 294
BASF Ultrason® E 2010 C6 30% Carbon Filled Carbon fibers and Ultrason® two partners with good properties. The combination of carbon fibers with the amorphous high-temperature plastic Ultrason® guarantees mechanical properties for temperatu..
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in
E-Polymers SEPAZ® LA40 PA66 LFT Resin Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and deliver..
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in
E-Polymers SEPAZ® LB40 PA6 LFT Resin Long Fiber Thermoplastics: SEPAZ LFT products, injection moldable long fiber-reinforced thermoplastics (LFT), are made using a unique pultrusion that thoroughly wets out the glass fibers and deliver..
Linear Mold Shrinkage, Transverse	0.0035 cm/cm	0.0035 in/in	LATI
LATI LASULF G/20 20% Glass Reinforced Polysulfone (PSU) (Unverified Data**) Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi..
Linear Mold Shrinkage, Transverse	0.0035 cm/cm @Time 86400 sec	0.0035 in/in @Time 24.0 hour	ISO 294
SABIC Innovative Plastics LNP THERMOCOMP GX94043L PSU (Europe-Africa-Middle East) LNP* THERMOCOMP* GX94043L is a compound based on Polysulfone resin containing Mineral.
Linear Mold Shrinkage, Transverse	0.0035 - 0.0050 cm/cm	0.0035 - 0.0050 in/in
LATI Lastane 50 G/25 PUR, 25% Glass Fiber Reinforced Polyurethane (PUR) based compound. Glass fibers. Very good noise reduction. Good impact resistance even at low temperature.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; No..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0055 cm/cm	0.0035 - 0.0055 in/in
LATI Latilon 28D G/30 PC, 30% Glass Fiber Reinforced Polycarbonate (PC) based compound. Glass fibers. Low smoke density and low toxicity index. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North A..
Linear Mold Shrinkage, Transverse	0.0035 - 0.0055 cm/cm	0.0035 - 0.0055 in/in
LATI Latilub 88/10-15T K/30 PEEK, 30% Carbon Fiber Reinforced, PTFE Filled Self-lubricating product based on Polyetheretherketone (PEEK). PTFE. Carbon fiber.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I..