Overview of materials for Polyphenylene Ether, 20% Glass Filled

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 20% Glass Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Ether, 20% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.15 - 1.32 g/cc
0.0415 - 0.0477 lb/in³
Average value: 1.21 g/cc Grade Count:29
Filler Content 20.0 %
20.0 %
Average value: 20.0 % Grade Count:5
Water Absorption 0.000 - 0.500 %
0.000 - 0.500 %
Average value: 0.0988 % Grade Count:17
Linear Mold Shrinkage 0.00200 - 0.00700 cm/cm
0.00200 - 0.00700 in/in
Average value: 0.00369 cm/cm Grade Count:24
Linear Mold Shrinkage, Transverse 0.00400 - 0.00800 cm/cm
0.00400 - 0.00800 in/in
Average value: 0.00580 cm/cm Grade Count:5
Melt Flow 1.00 - 20.0 g/10 min
1.00 - 20.0 g/10 min
Average value: 10.8 g/10 min Grade Count:9
Mechanical Properties Metric English Comments
Hardness, Rockwell R 106 - 118
106 - 118
Average value: 110 Grade Count:3
Tensile Strength, Ultimate 55.2 - 123 MPa
8000 - 17800 psi
Average value: 90.9 MPa Grade Count:24
20.0 - 70.0 MPa

@Temperature 60.0 - 120 °C
2900 - 10200 psi

@Temperature 140 - 248 °F
Average value: 44.2 MPa Grade Count:2
Tensile Strength, Yield 82.7 - 108 MPa
12000 - 15600 psi
Average value: 94.4 MPa Grade Count:8
Elongation at Break 1.00 - 10.0 %
1.00 - 10.0 %
Average value: 4.05 % Grade Count:22
2.00 - 4.00 %

@Temperature 60.0 - 120 °C
2.00 - 4.00 %

@Temperature 140 - 248 °F
Average value: 2.70 % Grade Count:2
Elongation at Yield 1.50 - 2.00 %

@Temperature 60.0 - 120 °C
1.50 - 2.00 %

@Temperature 140 - 248 °F
Average value: 1.70 % Grade Count:2
Modulus of Elasticity 3.10 - 7.00 GPa
450 - 1020 ksi
Average value: 6.21 GPa Grade Count:12
3.30 - 6.30 GPa

@Temperature 60.0 - 120 °C
479 - 914 ksi

@Temperature 140 - 248 °F
Average value: 5.17 GPa Grade Count:2
Flexural Yield Strength 96.5 - 194 MPa
14000 - 28200 psi
Average value: 130 MPa Grade Count:19
Flexural Modulus 3.20 - 6.21 GPa
464 - 900 ksi
Average value: 5.01 GPa Grade Count:25
Izod Impact, Notched 0.534 - 1.18 J/cm
1.00 - 2.20 ft-lb/in
Average value: 0.924 J/cm Grade Count:22
0.5339 - 0.90763 J/cm

@Temperature -40.0 - -30.0 °C
1.000 - 1.7004 ft-lb/in

@Temperature -40.0 - -22.0 °F
Average value: 0.692 J/cm Grade Count:3
0.600 - 0.700 J/cm

@Temperature -30.0 - 0.000 °C
1.12 - 1.31 ft-lb/in

@Temperature -22.0 - 32.0 °F
Average value: 0.692 J/cm Grade Count:1
0.600 - 0.700 J/cm

@Thickness 3.20 - 3.20 mm
1.12 - 1.31 ft-lb/in

@Thickness 0.126 - 0.126 in
Average value: 0.692 J/cm Grade Count:1
Izod Impact, Unnotched 3.20 - 5.34 J/cm
6.00 - 10.0 ft-lb/in
Average value: 4.76 J/cm Grade Count:7
Charpy Impact Unnotched 2.50 - 5.00 J/cm²
11.9 - 23.8 ft-lb/in²
Average value: 3.12 J/cm² Grade Count:5
2.50 - 2.50 J/cm²

@Temperature -20.0 - -20.0 °C
11.9 - 11.9 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 2.50 J/cm² Grade Count:2
Charpy Impact, Notched 0.600 - 1.40 J/cm²
2.86 - 6.66 ft-lb/in²
Average value: 0.830 J/cm² Grade Count:10
0.500 - 0.600 J/cm²

@Temperature -20.0 - -20.0 °C
2.38 - 2.86 ft-lb/in²

@Temperature -4.00 - -4.00 °F
Average value: 0.550 J/cm² Grade Count:2
Thermal Properties Metric English Comments
CTE, linear 36.0 - 50.0 µm/m-°C
20.0 - 27.8 µin/in-°F
Average value: 43.2 µm/m-°C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 127 - 254 °C
260 - 489 °F
Average value: 152 °C Grade Count:14
Deflection Temperature at 1.8 MPa (264 psi) 121 - 232 °C
250 - 450 °F
Average value: 140 °C Grade Count:27
Vicat Softening Point 130 - 200 °C
266 - 392 °F
Average value: 151 °C Grade Count:10
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:17
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+15 - 1.00e+17 ohm-cm
1.00e+15 - 1.00e+17 ohm-cm
Average value: 2.74e+16 ohm-cm Grade Count:14
Surface Resistance 10000 - 3.00e+14 ohm
10000 - 3.00e+14 ohm
Average value: 1.22e+14 ohm Grade Count:5
Dielectric Constant 2.00 - 3.20
2.00 - 3.20
Average value: 2.78 Grade Count:8
Dielectric Strength 16.5 - 70.0 kV/mm
420 - 1780 kV/in
Average value: 32.8 kV/mm Grade Count:8
Dissipation Factor 0.000800 - 0.00300
0.000800 - 0.00300
Average value: 0.00184 Grade Count:7
Comparative Tracking Index 175 - 250 V
175 - 250 V
Average value: 211 V Grade Count:6
Processing Properties Metric English Comments
Processing Temperature 232 - 282 °C
450 - 540 °F
Average value: 257 °C Grade Count:5
Nozzle Temperature 270 - 310 °C
518 - 590 °F
Average value: 290 °C Grade Count:3
Melt Temperature 249 - 316 °C
480 - 600 °F
Average value: 287 °C Grade Count:11
Mold Temperature 65.6 - 120 °C
150 - 248 °F
Average value: 86.5 °C Grade Count:16
Drying Temperature 80.0 - 110 °C
176 - 230 °F
Average value: 96.4 °C Grade Count:7
Injection Pressure 68.9 - 140 MPa
10000 - 20300 psi
Average value: 99.6 MPa Grade Count:8