- Polymer Property : Drying Temperature = 110 °C
Polymer Property : Drying Temperature = 110 °C Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Polykemi AB POLYblend 45FS GF20 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Polykemi AB POLYblend 45FS GK25 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Polykemi AB POLYblend 45FS GKF2505 PC/ABS-Blend, Glass Fiber reinforced Information provided by Polykemi AB |
|||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Polykemi AB POLYblend 65H PC/ABS-Blend Information provided by Polykemi AB |
|||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Polykemi AB POLYblend 85FS PC/ABS-Blend Information provided by Polykemi AB |
|||
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Polymer Resources PPX-FR3-[color]EN Modified PPO, UL 94 V-1 with HDT of 265 F, Extrusion Grade Process: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Polymer Resources PPX-FR7 Modified-PPO, V-0 Flame Retardant Modified-Polyphenylene Oxide, V-0 Flame Retardant, 260F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Polymer Resources PPX-G20 Modified-PPO, 20% Glass Reinforced Modified-Polyphenylene Oxide, 20% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Polymer Resources PPX-GP1 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 265F HDTFeatures: • Hydrolytically Stable • Low to No Water AbsorptionProcess: Injection MoldingNotes: All physical, mechanical and thermal testing.. |
|||
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Polymer Resources PPX-GP2 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 250F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Polymer Resources PPX-GP4 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 210F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
| Drying Temperature | 82.2 - 110 °C | 180 - 230 °F | |
| PolyOne Edgetek® PS-20CF/000 Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced
(discontinued **) Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Drying Temperature | 82.2 - 110 °C | 180 - 230 °F | 2 hrs |
| PolyOne Stat-Tech™ PS-18CF/000 CM Black Polybutylene Terephthalate (PBT), Carbon Fiber Reinforced
(discontinu Preliminary Data SheetDescription/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | Requested for non-reinforced self-extinguishing types. Temperature can be reduced when using vacuum ovens. |
| LATI LARIL 13 G/20 20% Glass Fiber Reinforced Polyphenylene Oxide (PPOm)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Lubrizol Advanced Materials Pearlthane® Clear 15N60D Thermoplastic Polyurethane
(discontinued **) Polyester-based TPU, supplied in form of translucent, colorless or slightly yellowish pellets, combining very high hardness with excellent mechanical properties and excellent hyrdrolysis resistance... |
|||
| Drying Temperature | 104 - 110 °C @Time 7200 - 14400 sec |
220 - 230 °F @Time 2.00 - 4.00 hour |
|
| Ravago Manufacturing Americas Hybrid S464LG Acrylonitrile Butadiene Styrene + PC Alloy Available in North America Good Toughness Low Gloss RoHS Compliant Form: Pellets Processing Method: Injection Molding Automotive Specifications: Chrysler MS-DB300 CPN4352 Color: Natural, Chry.. |
|||
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Kingfa PA66-G50 50% Glass Fiber Reinforced PA66 Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t.. |
|||
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Kingfa PA6-MG30 30% Glass & Mineral Filled PA6 Features:Low tendency to wrapExcellent size stabilityLow abrasionOutstanding surfaceApplications:Injection moldingAutomobile partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| LG Chemical LUCEL CF-620 Electrically Conductive POM, 20% Carbon Fiber Filled, High Strength, Wear Resistant LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| LG Chemical LUCEL MR-310 Low Warpage POM, 10% Mineral Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
| Drying Temperature | 100 - 110 °C @Time 14400 - 21600 sec |
212 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Kingfa MAC-551 PC/ABS Alloy Features:Excellent balance propertiesGood low temperature impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile license platePower toolComp.. |
|||
| Drying Temperature | 100 - 110 °C @Time 14400 - 21600 sec |
212 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Kingfa MAC-701 PC/ABS Alloy Features:Excellent balance propertiesHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelElectrical and electronic p.. |
|||
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Kingfa PA6-G30 N101 30% Glass Fiber Reinforced PA6 (general purpose) Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t.. |
|||
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Kingfa PA6-M20G16 20% Glass & 16% Mineral Filled PA6 Features:Low tendency to wrapExcellent size stabilityLow abrasionOutstanding surfaceApplications:Injection moldingAutomobile partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
| Drying Temperature | 79.4 - 110 °C @Time 10800 - 14400 sec |
175 - 230 °F @Time 3.00 - 4.00 hour |
Dehumidifying Dryer |
| Shuman 330 White PC/ABS Alloy Good impact strength, easy processability, good surface gloss, good chemical resistance Formerly Shuman 705 ABS/PC AlloyInformation provided by Shuman Plastics, Inc. |
|||
| Drying Temperature | 105 - 110 °C | 221 - 230 °F | |
| Celanese Hostaform® LX90Z POM, UV Resistant
(Unverified Data**) Hostaform® LX90Z specialty metallic appearance grades are an integrally colored nominal 9 melt flow rate based acetal copolymer material stabilized for use where ultraviolet radiation exposure is t.. |
|||
| Drying Temperature | 80.0 - 110 °C | 176 - 230 °F | Average value: 96.4 °C Grade Count:7 |
| Overview of materials for Polyphenylene Ether, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether, 20% Glass Filled". Specific grades with glass content between 15% and 24% are inclu.. |
|||
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | Requested for non-reinforced self-extinguishing types. Temperature can be reduced when using vacuum ovens. |
| LATI LARIL 13 G/30 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
| Drying Temperature | 95.0 - 110 °C @Time <=7200 sec |
203 - 230 °F @Time <=2.00 hour |
Dehumidifying dryer |
| Lehmann & Voss LUVOCOM® 1700-7903 PPO, with glass fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance r.. |
|||
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Polymer Resources PC/TP-GP3 PC Polyester, High Impact, Superior Chemical Resistance
(Unverified Data**)&l Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||