Ascend Performance Materials Vydyne® 47H BK03 Nylon 66, Impact Modified, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® 47H BK03 Nylon 66, Impact Modified, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® 47H BK03 is a general-purpose, impact-modified PA66 resin. Available in black, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 47H BK03 was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated. Vydyne 47H BK03 is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 47H BK03 is designed to meet the critical low-temperature impact requirements called out in many automotive specifications.Availability:Asia PacificEuropeNorth AmericaAdditive:Impact Modifier Features:Gasoline ResistanceGeneral Purpose Good Abrasion ResistanceGood Chemical Resistance Good ProcessabilityGood ToughnessHigh Impact ResistanceImpact ModifiedLow Temperature Impact Resistance Low Temperature ToughnessOil ResistantSolvent ResistantUses: Automotive ApplicationsConnectorsConsumer ApplicationsElectrical/Electronic ApplicationsFastenersGearsIndustrial Applications Appearance: BlackForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Water Absorption 1.2 %

@Time 86400 sec
 1.2 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 2.3 %
2.3 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.018 cm/cm

@Diameter 2.00 mm
 0.018 in/in

@Diameter 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Diameter 2.00 mm
 0.016 in/in

@Diameter 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
ISO 527-2
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-2
Elongation at Break >= 22 %
>= 22 %
ISO 527-2
Tensile Modulus 2.78 GPa
403 ksi
ISO 527-2
Flexural Strength 70.0 MPa
10200 psi
ISO 178
Flexural Modulus 2.30 GPa
334 ksi
ISO 178
Izod Impact, Notched (ISO) 12.0 kJ/m²

@Temperature -40.0 °C
 5.71 ft-lb/in²

@Temperature -40.0 °F
 ISO 180
16.0 kJ/m²

@Temperature -30.0 °C
 7.61 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
18.0 kJ/m²

@Temperature 23.0 °C
 8.57 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Charpy Impact Unnotched NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 ISO 179
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 1.10 J/cm²

@Temperature -40.0 °C
 5.23 ft-lb/in²

@Temperature -40.0 °F
 ISO 179
1.70 J/cm²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 ISO 179
1.90 J/cm²

@Temperature 23.0 °C
 9.04 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 11.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 6.11 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 14.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 7.78 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 185 °C
365 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 63.0 °C
145 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 75.0 °C

@Thickness 0.750 mm
 167 °F

@Thickness 0.0295 in
 UL 746
75.0 °C

@Thickness 1.50 mm
 167 °F

@Thickness 0.0591 in
 UL 746
75.0 °C

@Thickness 3.00 mm
 167 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 115 °C

@Thickness 0.750 mm
 239 °F

@Thickness 0.0295 in
 UL 746
115 °C

@Thickness 1.50 mm
 239 °F

@Thickness 0.0591 in
 UL 746
115 °C

@Thickness 3.00 mm
 239 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
Glow Wire Test 700 °C

@Thickness 0.750 mm
 1290 °F

@Thickness 0.0295 in
 Flammability Index; IEC 60695-2-12
700 °C

@Thickness 3.00 mm
 1290 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
725 °C

@Thickness 0.750 mm
 1340 °F

@Thickness 0.0295 in
 Ignition Temperature; IEC 60695-2-13
725 °C

@Thickness 3.00 mm
 1340 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
775 °C

@Thickness 1.50 mm
 1430 °F

@Thickness 0.0591 in
 Flammability Index; IEC 60695-2-12
800 °C

@Thickness 1.50 mm
 1470 °F

@Thickness 0.0591 in
 Ignition Temperature; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm

@Thickness 0.750 mm
 1.00e+11 ohm-cm

@Thickness 0.0295 in
 IEC 60093
Dielectric Strength 12.0 kV/mm

@Thickness 1.00 mm
 305 kV/in

@Thickness 0.0394 in
 IEC 60243
Arc Resistance 60 - 119 sec
60 - 119 sec
ASTM D495
Comparative Tracking Index 525 V

@Thickness 3.00 mm
 525 V

@Thickness 0.118 in
 IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.750 mm
 7.0 - 14 sec

@Thickness 0.0295 in
 UL 746
7.0 - 14 sec

@Thickness 1.50 mm
 7.0 - 14 sec

@Thickness 0.0591 in
 UL 746
15 - 29 sec

@Thickness 3.00 mm
 15 - 29 sec

@Thickness 0.118 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 UL 746
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 25.5 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 310 °C
536 - 590 °F
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Front Barrel Temperature 280 - 310 °C
536 - 590 °F
Nozzle Temperature 280 - 310 °C
536 - 590 °F
Melt Temperature 285 - 305 °C
545 - 581 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %