SABIC Innovative Plastics LNP LUBRILOY D2000I PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY D2000I PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRILOY* D2000I is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, High Impact.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | ASTM D638 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Elongation at Yield | 5.6 % | 5.6 % | ASTM D638 |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 7.79 J/cm | 14.6 ft-lb/in | ASTM D256 |
| 5.42 J/cm <br>@Temperature -40.0 °C |
10.2 ft-lb/in <br>@Temperature -40.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 17.62 J/cm | 33.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 43.0 kJ/m² <br>@Temperature -40.0 °C |
20.5 ft-lb/in² <br>@Temperature -40.0 °F |
80*10*4; ISO 180/1A |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.22 | 0.22 | ASTM D3702 Modified |
| K (wear) Factor | 70.5 x 10<sup>-8</sup> mm³/N-M | 35.0 x 10<sup>-10</sup> in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.1 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
44.5 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 131 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
72.8 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 85.4 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
47.4 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 135 µm/m-°C <br>@Temperature -40.0 - 40.0 °C |
75.0 µin/in-°F <br>@Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C <br>@Thickness 3.20 mm |
248 °F <br>@Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Permabond 101 Cyanoacrylate, Wicking Viscosity
- Pinnacle Polymers 1335 Z Polypropylene Homopolymer, Injection Molding Grade, Nucleated, with Antistat
- PolyOne Nymax™ GF 1200 A 55 HS Natural Polyamide 66 (Nylon 66)
- Freudenberg Simrit V60 Standard Fluoroelastomer
- Materion BrushCAST® 20C High Strength Casting Alloy (Solution Annealed & Aged)
- H.C. Starck Amperit® 105.2 Agglomerated Sintered Molybdenum (Mo)
- Styrolution Terblend® N NM-21 EF Gray 38058 ABS+PA (Dry)
- Dow Corning 3581 Performance Modifier
Copyright © lookpolymers.com All Rights Reserved