- Polypropylene with 20% Talc Filler
- RheTech Products HP531-00 22% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
RheTech Products HP531-00 22% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products HP531-00 22% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: IP structural componentsAir ducts - distributionA/B/C/ PillarsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 22 % | 22 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Melt Flow | 23 g/10 min @Load 2.16 kg, Temperature 230 °C |
23 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 71 | 71 | ASTM D2240 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.14 GPa | 310 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 23.0 °C |
0.800 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 6.78 J | 5.00 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 112 °C | 234 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.8 °C | 154 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Nozzle Temperature | 216 - 227 °C | 420 - 440 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- ExxonMobil HD 6761.17 Injection Molding Resin (discontinued **)
- LG Chemical LUMID HI5063A(W) PA6/ABS+MF6%, High Impact
- Greene Tweed CHEMRAZ® 618 Perfluoroelastomer
- Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours
- A. Schulman ComAlloy® E-12812 Easy Flow Glass Reinforced Nylon 66
- Unipetrol PP MONSTEN® GB 608 Polypropylene Impact Copolymer
- CoorsTek ACI-Ni6 Tungsten Carbide
- Dow Corning 360 Medical Fluid, 20 CST.
- Huntsman Rexell® H2103 Injection Molding LLDPE (discontinued **)
- E-Polymers EFLEX® I2040 Ionomer
Copyright © lookpolymers.com All Rights Reserved