Toyobo GLAMIDE® T-422-02 Nylon-6

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled
Manufacturer	Toyobo
Trade Name	GLAMIDE®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Toyobo GLAMIDE® T-422-02 Nylon-6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade T-422-02 is a mineral-reinforced Nylon-6 with high heat resistance and high rigidity.35

Physical Properties	Metric	English	Comments
Specific Gravity	1.42 g/cc	1.42 g/cc	Absolute Drying; ASTM-D792
Filler Content	35 %	35 %
Water Absorption	0.70 %	0.70 %	Absolute Drying; ASTM-D570
Moisture Absorption at Equilibrium	2.3 %	2.3 %	Absolute Drying; ASTM-D570
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm @Thickness 1.00 mm	0.0010 - 0.0020 in/in @Thickness 0.0394 in	Absolute Drying
	0.0030 - 0.0060 cm/cm @Thickness 3.00 mm	0.0030 - 0.0060 in/in @Thickness 0.118 in	Absolute Drying
Melt Flow	3.0 g/10 min	3.0 g/10 min

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	Absolute Drying; ASTM-D785
Tensile Strength, Ultimate	40.0 MPa @Temperature 80.0 °C	5800 psi @Temperature 176 °F	Practical Use (Water Absorption 2.3%); ASTM-D638
	50.0 MPa @Temperature 80.0 °C	7250 psi @Temperature 176 °F	Absolute Drying; ASTM-D638
	65.0 MPa @Temperature 23.0 °C	9430 psi @Temperature 73.4 °F	Practical Use (Water Absorption 2.3%); ASTM-D638
	95.0 MPa @Temperature 23.0 °C	13800 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D638
	115 MPa @Temperature -40.0 °C	16700 psi @Temperature -40.0 °F	Practical Use (Water Absorption 2.3%); ASTM-D638
	120 MPa @Temperature -40.0 °C	17400 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D638
Elongation at Break	3.2 %	3.2 %	Absolute Drying; ASTM-D638
	5.0 %	5.0 %	Practical Use (Water Absorption 2.3%); ASTM-D638
Flexural Strength	55.0 MPa @Temperature 80.0 °C	7980 psi @Temperature 176 °F	Practical Use (Water Absorption 2.3%); ASTM-D790
	80.0 MPa @Temperature 80.0 °C	11600 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
	96.0 MPa @Temperature 23.0 °C	13900 psi @Temperature 73.4 °F	Practical Use (Water Absorption 2.3%); ASTM-D790
	145 MPa @Temperature 23.0 °C	21000 psi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
	165 MPa @Temperature -40.0 °C	23900 psi @Temperature -40.0 °F	Practical Use (Water Absorption 2.3%); ASTM-D790
	175 MPa @Temperature -40.0 °C	25400 psi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Flexural Modulus	1.70 GPa @Temperature 80.0 °C	247 ksi @Temperature 176 °F	Practical Use (Water Absorption 2.3%); ASTM-D790
	4.00 GPa @Temperature 80.0 °C	580 ksi @Temperature 176 °F	Absolute Drying; ASTM-D790
	5.00 GPa @Temperature 23.0 °C	725 ksi @Temperature 73.4 °F	Practical Use (Water Absorption 2.3%); ASTM-D790
	7.30 GPa @Temperature 23.0 °C	1060 ksi @Temperature 73.4 °F	Absolute Drying; ASTM-D790
	7.50 GPa @Temperature -40.0 °C	1090 ksi @Temperature -40.0 °F	Practical Use (Water Absorption 2.3%); ASTM-D790
	8.60 GPa @Temperature -40.0 °C	1250 ksi @Temperature -40.0 °F	Absolute Drying; ASTM-D790
Compressive Strength	69.0 MPa	10000 psi	Practical Use (Water Absorption 2.3%); ASTM-D695
	100 MPa	14500 psi	Absolute Drying; ASTM-D695
Izod Impact, Notched	0.580 J/cm @Temperature -40.0 °C	1.09 ft-lb/in @Temperature -40.0 °F	Absolute Drying; ASTM-D256
	0.700 J/cm @Temperature -40.0 °C	1.31 ft-lb/in @Temperature -40.0 °F	Practical Use (Water Absorption 2.3%); ASTM-D256
	0.950 J/cm @Temperature 23.0 °C	1.78 ft-lb/in @Temperature 73.4 °F	Absolute Drying; ASTM-D256
	2.70 J/cm @Temperature 23.0 °C	5.06 ft-lb/in @Temperature 73.4 °F	Practical Use (Water Absorption 2.3%); ASTM-D256
Taber Abrasion, mg/1000 Cycles	30	30	CS-17, Absolute Drying; ASTM-D1044

Thermal Properties	Metric	English	Comments
CTE, linear	45.0 µm/m-°C	25.0 µin/in-°F	Absolute Drying; ASTM-D696
Deflection Temperature at 0.46 MPa (66 psi)	210 °C	410 °F	Absolute Drying; ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi)	175 °C	347 °F	Absolute Drying; ASTM-D648
Flammability, UL94	HB	HB

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+9 ohm-cm	1.00e+9 ohm-cm	Practical Use (Water Absorption 2.3%); ASTM-D257
	1.00e+12 ohm-cm	1.00e+12 ohm-cm	Absolute Drying; ASTM-D257
Dielectric Strength	20.0 kV/mm @Thickness 2.00 mm	508 kV/in @Thickness 0.0787 in	Practical Use (Water Absorption 2.3%); ASTM-D149
	29.0 kV/mm @Thickness 2.00 mm	737 kV/in @Thickness 0.0787 in	Absolute Drying; ASTM-D149
Arc Resistance	120 sec	120 sec	Practical Use (Water Absorption 2.3%); ASTM-D495
	130 sec	130 sec	Absolute Drying; ASTM-D495
Comparative Tracking Index	>= 600 V	>= 600 V	IEC Method

Processing Properties	Metric	English
Melt Temperature	260 - 290 °C	500 - 554 °F
Mold Temperature	60.0 - 100 °C	140 - 212 °F
Injection Pressure	40.0 - 80.0 MPa	5800 - 11600 psi