Polymer Property : Flexural Strength = 21000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 145 MPa

@Temperature 175 °C
21000 psi

@Temperature 347 °F
ISO 178
Victrex® WG102™ Polyaryletherketone
Product Description: High performance thermoplastic material, PolyArylEtherKetone (PAEK), semi crystalline, granules for injection moulding, standard flow, FDA food contact compliantWG102 does not c..
Flexural Strength 145 MPa

@Thickness 1.57 mm
21000 psi

@Thickness 0.0620 in
LW; ASTM D790
Industrial Laminates/Norplex NP842 Paper Base Laminate  (discontinued **)
Description: Paper reinforced phenolic grade with controlled conductivity. Mechanical strength similar to NP611. NP842 is semi-conductive on the surfaces and through the laminate.Thickness Tested: 0..
Flexural Strength 145 MPa

@Thickness 1.57 mm
21000 psi

@Thickness 0.0620 in
LW; ASTM D790
Industrial Laminates/Norplex NP347 Cotton Fabric
Description: Bleached canvas with high temperature phenolic resin with molybdenum disulfide lubricant. Low moisture absorption. Capable of 150°C continuous operation.Thickness Tested: 0.062", 0.1..
Flexural Strength 145 MPa

@Thickness 1.57 mm
21000 psi

@Thickness 0.0620 in
CW; ASTM D790
Industrial Laminates/Norplex NP843 Paper Base Laminate
Description: Paper reinforced phenolic grade with controlled conductivity. Mechanical strength similar to NP611. NP843 has conductive surfaces only, as compared to NP842, which is conductive through..
Flexural Strength 145 MPa

@Strain 6.30 %
21000 psi

@Strain 6.30 %
cond., 2 mm/min; ISO 178-A
Lanxess Durethan® BKV 130 GIT DUS008 900116 Nylon 6, Impact Modified
PA 6, 30% glass fibers, injection molding, impact modified, GIT/WITInformation provided by LANXESS.
Flexural Strength 145 MPa

@Temperature 23.0 °C
21000 psi

@Temperature 73.4 °F
Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-422-02 Nylon-6
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength 145 MPa

@Temperature -40.0 °C
21000 psi

@Temperature -40.0 °F
Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-808-02 Nylon-6
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength 145 MPa

@Temperature 23.0 °C
21000 psi

@Temperature 73.4 °F
Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-502NZ 6T-Nylon
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength 145 MPa

@Temperature -40.0 °C
21000 psi

@Temperature -40.0 °F
ASTM D790
BASF Ultramid® 8281 HS GP PA6 (Conditioned)
Description: Ultramid 8281 HS GP is an unreinforced, heat stabilized PA6 rot molding compound. It is available in natural and black and can be painted. It exhibits excellent balance of engineering p..