Polymer Property : Flexural Strength = 80.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	80.0 MPa @Temperature 23.0 °C	11600 psi @Temperature 73.4 °F	ASTM D790
DuPont Performance Polymers Crastin® 6130 NC010 PBT (Unverified Data**) Crastin® 6130 NC010 is an unreinforced, medium high viscosity polybutylene terephthalate resin for extrusion and injection molding.Information provided by DuPont Performance Polymers
Flexural Strength	80.0 MPa @Temperature 125 °C	11600 psi @Temperature 257 °F	Result based on 450G; ISO 178
Victrex® PEEK 600G Polyetheretherketone (discontinued **) Product Description: High performance thermoplastic material, unreinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, low viscosity, FDA food conta..
Flexural Strength	80.0 MPa @Temperature 175 °C	11600 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 450FC30 General Purpose Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and ext..
Flexural Strength	80.0 MPa @Temperature 175 °C	11600 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 450GL30 30% Glass Fiber Reinforced Product Description: High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection molding and extrusion, standard flow, F..
Flexural Strength	80.0 MPa @Temperature 175 °C	11600 psi @Temperature 347 °F	Result based on 450GL30; ISO 178
Victrex® PEEK 450GL30 Polyetheretherketone, 30% Glass Fiber, Black Product Description: High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, Standard viscos..
Flexural Strength	80.0 MPa @Temperature 23.0 °C	11600 psi @Temperature 73.4 °F	DAM; ISO 178
DuPont Performance Polymers Zytel® 157HSL BK010 Nylon 612 (Unverified Data**) Zytel® 157HSL BK010 is a heat stabilized, weatherable, lubricated polyamide 612 resin that is suitable for molding and extrusion applications.Information provided by DuPont Performance Polymers
Flexural Strength	80.0 MPa @Strain 7.00 %	11600 psi @Strain 7.00 %	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified PA 6-Copolymer, 15% glass fibers, injection molding impact modifiedInformation provided by LANXESS.
Flexural Strength	80.0 MPa @Temperature 23.0 °C	11600 psi @Temperature 73.4 °F	Practical Use (Water Absorption 3.0%); ASTM-D790
Toyobo GLAMIDE® T-400G15 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	80.0 MPa @Temperature 80.0 °C	11600 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® T-422-02 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	80.0 MPa @Temperature 80.0 °C	11600 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-502NZ 6T-Nylon GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	80.0 MPa @Temperature 80.0 °C	11600 psi @Temperature 176 °F	Absolute Drying; ASTM-D790
Toyobo GLAMIDE® TY-835TC Nylon-66 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a..
Flexural Strength	80.0 MPa @Treatment Temp. 150 °C, Time 3600 sec	11600 psi @Treatment Temp. 302 °F, Time 1.00 hour	ISO 178; IEC/EN 60893-2 5.1
Elektro-Isola G-Etronax PM GPO 3 Polyester, Glass Mat, Red, Sheets Description: Good electrical properties such as high breakdown voltage in air and oil and highest arc resistance and tracking resistance. Self-extinguishing. Low smoke emission, halogen-free.Applica..
Flexural Strength	80.0 MPa @Strain 3.50 %, Temperature 23.0 °C	11600 psi @Strain 3.50 %, Temperature 73.4 °F	ISO 178
DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and mod..
Flexural Strength	80.0 MPa @Temperature 175 °C	11600 psi @Temperature 347 °F	ISO 178
Victrex® PEEK 150FC30 Easy Flow Product Description: High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy ..