- Polymer Property : CTE, linear = 25.0 µin/in-°F
Polymer Property : CTE, linear = 25.0 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 45.0 µm/m-°C @Temperature -40.0 - 149 °C |
25.0 µin/in-°F @Temperature -40.0 - 300 °F |
ASTM E831 |
| Quadrant EPP Techtron® PSGF PPS - Compression Molded 40% Glass Reinforced Polyphenylene Sulfide (ASTM Product Data Sheet) |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | |
| Permabond ES558 Epoxy Resin PERMABOND ES558 is a single-part epoxy paste which flows like solder when heated during curing. The adhesive is toughened for maximum impact resistance, along with excellent peel and shear strength... |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM E228 |
| Solvay Engineered Polymers SEQUEL® 2382 Engineered Polyolefin
(discontinued **) Description: SEQUEL® 2382 engineered polyolefin is designed for large mold-in-color interior applications that require stiffness and dimensional stability. This material exhibits excellent process.. |
|||
| CTE, linear | 45.0 - 90.0 µm/m-°C | 25.0 - 50.0 µin/in-°F | Average value: 63.7 µm/m-°C Grade Count:46 |
| Overview of materials for PVC, Extruded This property data is a summary of similar materials in the MatWeb database for the category "PVC, Extruded". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
| CTE, linear | 45.0 - 70.0 µm/m-°C | 25.0 - 38.9 µin/in-°F | Average value: 55.4 µm/m-°C Grade Count:6 |
| Overview of materials for Polychlorotrifluoroethylene; Molded This property data is a summary of similar materials in the MatWeb database for the category "Polychlorotrifluoroethylene; Molded". Each property range of values reported is minimum and maximum valu.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
Vertical Direction; ASTM D696 |
| Mitsui Arlen™ A335 35% Glass Fiber-Reinforced Modified Nylon 6T (COND) ARLEN™ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320°C) and a rigidity level comparable to super engineering plastics, it poss.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| LyondellBasell Hifaxâ„¢ CJ232 Thermoplastic Olefin Resin Key Features: medium high melt flow, medium modulus, low CLTE, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, paintableApplicat.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| LyondellBasell Hostacomâ„¢ CB271FC Thermoplastic Polyolefin Elastomer Description: Hostacomâ„¢ CB271FC high melt flow, 2,400 MPa flexural modulus, precolored, UV-stabilized, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent combination of.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 23.9 - 260 °C |
25.0 µin/in-°F @Temperature 75.0 - 500 °F |
ASTM E831 |
| Saint-Gobain Meldin® 7021 Isostatically Molded Graphite Filled Polyimide Melidin® 7021 is a self-lubricating thermosetting polyimide that contains 15% graphite filler. Melidin® 7021 has a low coefficient of friction and high heat resistance, and is best for high t.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| SABIC Innovative Plastics NORYL PX4716 PPE+HIPS (Asia Pacific) PPE+PS GF15% FR V-1 |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer DescriptionPolytrope TPP 608 is an olefinic elastomer exhibiting low thermal expansion, low heat sag and high DOI on painted parts. ApplicationTPP 608 is designed specifically for automotive fascia.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 176 °F |
Borealis Method |
| Borealis Daplen™ EF210AE Polypropylene TPO Compound Daplen™ EF210AE is a 20% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, gives a good surface q.. |
|||
| CTE, linear | 45.0 - 50.0 µm/m-°C | 25.0 - 27.8 µin/in-°F | |
| Master Bond UV10TKMed One component UV curable, biocompatible, high viscosity compound Product Description: Master Bond UV10TKMed is a higher viscosity, one part UV system for bonding, sealing and coating that passes USP Class VI testing along with ISO 10993-5 for cytotoxicity. It has.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer DescriptionPolytrope TPP 608 is an olefinic elastomer exhibiting low thermal expansion, low heat sag and high DOI on painted parts. ApplicationTPP 608 is designed specifically for automotive fascia.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Toyobo ECOVYLOPET® EMC2301E PET Bottle Recycling Grade, 15% Filler Reinforced Features: PET Bottle Recycling Grade, 15% Filler Reinforced, Modified TypeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Toyobo T-422-02R Nylon, Mineral-Reinforced Key Feature: High heat distortion and good toughness, high flowInformation provided by Toyobo Co., Ltd |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature -30.0 - 100 °C |
25.0 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer DescriptionPolytrope TPP 608 is an olefinic elastomer exhibiting low thermal expansion, low heat sag and high DOI on painted parts. ApplicationTPP 608 is designed specifically for automotive fascia.. |
|||
| CTE, linear | 45.0 - 50.0 µm/m-°C | 25.0 - 27.8 µin/in-°F | |
| Master Bond EP30M4 Chemically Resistant Two Component Epoxy System Master Bond Polymer System EP30M4 is a two component epoxy system for high performance bonding, sealing and encapsulation. This system features a forgiving 100 to 60 mix ratio by weight. EP30M4 resi.. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | Below Tg |
| Tra-Con Tra-Bond 9070D Filled Epoxy Adhesive TRA-BOND 9070D filled epoxy adhesive exhibits a low coefficient of expansion. Information provided by Tra-Con Inc. |
|||
| CTE, linear | 45.0 - 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.0 - 38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ASTM D696 |
| Daikin NEOFLON M-300P PCTFE Pellets NEOFLON PCTFE M-300 series is used for general purpose applications.Description:Pellets.Processing Methods: Extrusion.Uses: Rods, small parts.Information provided by Daikin Industries. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | Below Tg |
| Epoxy Technology EPO-TEK® OD2002 High Temperature Epoxy Material Description: High Tg version of EPO-TEK®353ND with low modulus and good toughness. Replacement for EPO-TEK® 364. Complies with USP Class VI biocompatibility standards.Information Provid.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Asahi Kasei Thermylene® P1-35FM-1374H 35% Glass/Fiber Reinforced Information provided by Asahi Thermofil |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Asahi Kasei Thermofil N-13FG-1626 13% Glass Fiber Reinforced, Heat Stabilized Information provided by Asahi Thermofil |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Asahi Kasei Thermylene® P1-20FG-2703 20% Glass Fiber Reinforced, Impact Modified Information provided by Asahi Thermofil |
|||
| CTE, linear | 45.0 - 220 µm/m-°C | 25.0 - 122 µin/in-°F | Average value: 143 µm/m-°C Grade Count:24 |
| Overview of materials for Polyether Ester Elastomer This property data is a summary of similar materials in the MatWeb database for the category "Polyether Ester Elastomer". Each property range of values reported is minimum and maximum values of appr.. |
|||
| CTE, linear | 45.0 µm/m-°C | 25.0 µin/in-°F | ASTM E831 |
| Addiplast Addinyl C2 V20 Nylon 66/6, 20% Glass Filled Glass fiber reinforced, high strengthInformation provided by Addiplast. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CENTROPLAST CENTRO HPM Polyetherimide This material has high strength and rigidity at high temperatures, with good electrical properties. Applications include electrical insulators, and load-bearing components.Information provided by C.. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Cosmic Plastics D44 Mineral Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
| CTE, linear | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
|
| Loctite® 3880 Heat Cure Isotropic Epoxy Adhesive Electrically Conductive BondersLoctite® Electrically Conductive Adhesives are used in a variety of applications where electrical connectivity is needed, providing a conductive path where traditiona.. |
|||