RheTech Products FT4802-692UV Thermoplastic Polyolefin, UV Stabilized, RS8 Grey

Category Polymer , Thermoplastic , Polyolefin
Manufacturer RheTech Products
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RheTech Products FT4802-692UV Thermoplastic Polyolefin, UV Stabilized, RS8 Grey.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products.
Physical Properties Metric English Comments
Specific Gravity 1.01 g/cc
1.01 g/cc
23/23°C; ASTM D792
Filler Content 16 %
16 %
ASTM D5630
Linear Mold Shrinkage 0.0095 cm/cm
0.0095 in/in
ASTM D955
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 230 °C
15 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 64
64
ASTM D2240
Tensile Strength at Break 17.9 MPa
2600 psi
2 in/min; ASTM D638
Flexural Modulus 1.24 GPa
180 ksi
Tangent; ASTM D790
Izod Impact, Notched 8.01 J/cm

@Temperature 23.0 °C
15.0 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Gardner Impact 15.9 J
11.7 ft-lb
ASTM D5420
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 107 °C
225 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 199 - 227 °C
390 - 440 °F
Middle Barrel Temperature 204 - 232 °C
400 - 450 °F
Front Barrel Temperature 210 - 238 °C
410 - 460 °F
Nozzle Temperature 216 - 227 °C
420 - 440 °F
Mold Temperature 26.7 - 48.9 °C
80.0 - 120 °F
Drying Temperature 65.6 - 82.2 °C
150 - 180 °F
Dry Time 1 - 2 hour
1 - 2 hour
Moisture Content <= 0.050 %
<= 0.050 %
Recommended
Injection Pressure 55.2 - 103 MPa
8000 - 15000 psi
Hold Pressure 27.6 - 51.7 MPa
4000 - 7500 psi
Back Pressure 0.345 - 1.03 MPa
50.0 - 150 psi