Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 17.9 MPa | 2600 psi | Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable EC486 DA Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications.Information provided by PolyOne |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT1004-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT1004-625UV Thermoplastic Polyolefin, UV Stabilized, Interior DX9 Black Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT2400-648UV Thermoplastic Polyolefin, UV Stabilized, 848 Black Applications: Bumper rub stripsHitch padsScuff padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT3080-425 Thermoplastic Polyolefin, UV Stabilized, YBWA Platinum Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT3080-640UV Thermoplastic Polyolefin, UV Stabilized, BFQA Arizona Beige Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT3080-727UV Thermoplastic Polyolefin, UV Stabilized, G01 Black Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT3080-729UV Thermoplastic Polyolefin, UV Stabilized, AG-64 Grey Applications: Step padsHitch padsScuff platesInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT3080-757UV Thermoplastic Polyolefin, UV Stabilized, Pueblo Gold Applications: Step padsHitch padsScuff padsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT4700-01A Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: CladdingsBodyside moldingsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT4802-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT4802-690UV Thermoplastic Polyolefin, UV Stabilized, HS5 Medium Dark Neutral Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT4802-690UVA Thermoplastic Polyolefin, UV Stabilized, HS5 Medium Dark Neutral Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT4802-692UV Thermoplastic Polyolefin, UV Stabilized, RS8 Grey Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT4802-693UV Thermoplastic Polyolefin, UV Stabilized, SPN Dark Teal Applications: Bodyside moldings and claddingsFacia and bumper coversExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products FT7011-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black Applications: Claddings and faciasExterior componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa @Temperature 23.0 °C |
2600 psi @Temperature 73.4 °F |
Die C2 hr; ASTM D412 |
PolyOne OnFlex™ AW 300-02 Thermoplastic Elastomer (TPE) OnFlex™ AW 300-02 is a non-halogen flame retardant material designed for appliance wire applications. New Product. Commercial specifications have not been established.Purge thoroughly before and af.. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | 2 in/min; ASTM D638 |
RheTech Products UVFT3082-74 Thermoplastic Polyolefin, 135K Flexural Modulus, UV Stabilized, Exterior DX9 Black Applications: Step padsHitch padsExterior trimInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | |
NEU Neuthane N8511-1H Aromatic, Polyester TPU Blend A blend of aromatic, polyester TPUs with good clarity |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | molding; ASTM D638 |
LyondellBasell Petrothene® NA942000 Low Density Polyethylene, Film Extrusion Grade PETROTHENE NA942 is a series of resins designed especially for heavy duty film applications, such as bags used to package fertilizer, peat moss, decorative stone and agricultural and construction ma.. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D638 |
Teknor Apex APEX® 85-J644Z-3 Polyvinyl Chloride, Flexible Notes: 105°C Jacket Forms: Pellets Agency Ratings: UL 13; UL 1424; UL 1655; UL 2250; UL 444 Wire Types: CATV; CL3; CMX; CL2; CM; FT-4Information Provided by Teknor Apex |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D638 |
Teknor Apex APEX® 97-G0029C-82 Polyvinyl Chloride, Flexible Notes: 80°C Jacket; RoHS CompliantFeatures: Flame Retardant Uses: Cable Jacketing; Communication Wire JacketingAgency Ratings: UL 62; UL 444 Forms: Pellets Processing Method: ExtrusionInformation.. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 524E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524E is an extrusion grade olefinic thermoplastic elastomer. This mineral filled product is suited for profile extrusion or blow molding. TPP 524E is paintable and can be .. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D638 |
A. Schulman POLYTROPE™ TPP 524E Extrusion Grade Olefinic Thermoplastic Elastomer DescriptionPolytrope TPP 524E is an extrusion grade olefinic thermoplastic elastomer. This mineral filled product is suited for profile extrusion or blow molding. TPP 524E is paintable and can be .. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D 638 |
RTP Company RTP 199 X 137777 C Polypropylene (PP) Co-Polymer - High Flow - High Impact - Flame Retardant - UV Stabilized |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D412 |
Teknor Apex Telcar® TL-2468A Thermoplastic Elastomer Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets .. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | at 2.0 in/min, Tested using a 50 mil. Sheet; ASTM D638 |
Chevron Phillips EB6755 Rubber Modified Polystyrene DescriptionChevron EB6755 is an extrusion grade, high impact polystyrene developed for use in packaging applications. It is designed for exceptional environmental stress-crack resistance and practi.. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
Dow DMDA-8980 NT 7 High Density Polyethylene Resin DOW DMDA-8980 NT 7 is produced using UNIPOL™ process technology. It is intended for use in thin wall injection molding applications such as food containers. Information provided by Dow |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | Press Cure 15 minutes @ 177°C, Post Cure 24 hours @ 260°C |
3M Dyneon™ FLS 2650 Fluoroelastomer 3M™ Dyneon™ Fluoroelastomer FLS 2650 can be compounded using standard water cooled internal mixers or two-roll mills with standard fillers and ingredients utilized in typical fluoroelastomer formu.. |
|||
Tensile Strength at Break | 17.9 MPa | 2600 psi | Press cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D412 |
3M Dyneon™ PFE 60Z Perfluoroelastomer Dyneon™ PFE 60 Z is a technically advanced peroxide curable perfluoroelastomer, designed to meet the challenges of demanding sealing applications. It’s fully fluorinated back bone structure provid.. |