E-Polymers SEPAZ® N4040M1 Dimensional Stability Heat Resistance Nano Composite Resin

Category Polymer , Thermoplastic
Manufacturer E-Polymers Co. Ltd.
Trade Name SEPAZ®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF E-Polymers SEPAZ® N4040M1 Dimensional Stability Heat Resistance Nano Composite Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nanocomposite: SEPAZ Nano PA6 nanocomposites have been prepared successfully in commercial scale through 'in situ' polymerization or melt extrusion. The unique performance properties of nanocomposities provide a great flexibility in materials design. Nanocomposites have been formulated into various resin systems to deliver desired properties: from rheology control to fire retardation. It shows low specific gravity, gas permeability and high heat resistance, rigidity, dimension stability used for underhood and fuel line parts in automotive industry and for packaging film in food industry.Information Provided by E-Polymers Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Water Absorption 0.40 %

@Time 86400 sec
0.40 %

@Time 24.0 hour
Linear Mold Shrinkage 0.0060 cm/cm
0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength 88.78 MPa
12880 psi
ASTM D638
Elongation at Break 1.1 %
1.1 %
ASTM D638
Flexural Strength 125.08 MPa
18141 psi
ASTM D790
Flexural Modulus 8.564 GPa
1242 ksi
ASTM D790
Izod Impact, Notched 0.353 J/cm
0.661 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 165 °C
329 °F
ASTM D648
Flammability, UL94 HB
HB
Processing Properties Metric English Comments
Melt Temperature 227 °C
441 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F