Polymer Resources AH-GP2-TFE10 Acetal Homopolymer, 10% PTFE

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, PTFE-Filled
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources AH-GP2-TFE10 Acetal Homopolymer, 10% PTFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
ASTM D792
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Melt Flow 7.0 - 13 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 - 13 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.6 MPa
8500 psi
ASTM D638
Tensile Strength, Yield 58.6 MPa
8500 psi
ASTM D638
Flexural Strength 89.6 MPa
13000 psi
ASTM D790
Flexural Modulus 2.93 GPa
425 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature 22.8 °C
1.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 163 °C
325 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 98.9 °C
210 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 193 - 204 °C
380 - 400 °F
Middle Barrel Temperature 196 - 207 °C
385 - 405 °F
Front Barrel Temperature 199 - 210 °C
390 - 410 °F
Melt Temperature 193 - 216 °C
380 - 420 °F
Mold Temperature 79.4 - 104 °C
175 - 220 °F
Drying Temperature 76.7 - 82.2 °C
170 - 180 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0005