Polymer Property : Linear Mold Shrinkage = 0.021 cm/cm Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0080 - 0.021 cm/cm
0.0080 - 0.021 in/in
FRISETTA Test Method
Nilit FRIANYL A63 CV-CM 0830 9005/Z Powder-coatable nylon 6.6 for injection molding, 8% carbon fiber reinforced, 30% ceramic filled
Powder-coatable nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Linear Mold Shrinkage 0.014 - 0.021 cm/cm
0.014 - 0.021 in/in
FRISETTA Test Method
Nilit FRIANYL A63 S15 Nylon 6.6 for injection molding
Nylon 6.6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Linear Mold Shrinkage 0.014 - 0.021 cm/cm
0.014 - 0.021 in/in
FRISETTA Test Method
Nilit FRIANYL A63 S20 Nylon 6.6 for injection molding
Nylon 6.6 for injection molding, impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AC-GP2-TFE5 Acetal Copolymer, 5% PTFE
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AH-GP1 Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AH-GP2 Acetal Homopolymer, Medium Flow, Heat Stabilized
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AH-GP2-TFE10 Acetal Homopolymer, 10% PTFE
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin, Heat Stabilized
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.015 - 0.021 cm/cm
0.015 - 0.021 in/in
Across Flow; ASTM D955
Polymer Resources NY66-GP2 General Purpose Nylon 66, Nucleated
General Purpose Nylon 66, Nucleated Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry..
Linear Mold Shrinkage 0.011 - 0.021 cm/cm
0.011 - 0.021 in/in
FRISETTA Test Method
Nilit FRIANYL C73 T Nylon 6.6/6 for injection molding
Nylon 6.6/6 for injection molding, medium viscosity, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.015 - 0.021 cm/cm
0.015 - 0.021 in/in
Lehmann & Voss LUVOCOM® 80-7580/BK Polyacetal-copolymer, with aramid reinforcement and PTFE
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL EC-605B Electrically Conductive POM, 5% Carbon Black Filled
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL N109-02 General Purpose POM, Unreinforced, Externally Lubricated, Standard Viscosity
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL N115 POM, Unreinforced, High Viscosity
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL N115-LD Anti Mold Deposit POM, Unreinforced, Internally Lubricated, Standard Viscosity
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL N127-02 General Purpose POM, Unreinforced, Externally Lubricated, High Flow
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL N127-AS Antistatic POM, Unreinforced, High Flow
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL N145-AS Antistatic POM, Unreinforced, Internally Lubricated, Ultra High Flow
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL VC127-LD Antistatic POM, Unreinforced, High Flow, For VCR Reels
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL VC-145 Antistatic POM, Unreinforced, Ultra High Flow, For VCR Reels
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical LUCEL WK-320 Wear Resistant POM, 20% Mineral Filled, High Modulus
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
LG Chemical Lucet® N127 Acetal Copolymer
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
Linear Mold Shrinkage 0.012 - 0.021 cm/cm
0.012 - 0.021 in/in
ASTM D955
LG Chemical Lupox® PBT-GP-1000 High Flow PBT
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
Linear Mold Shrinkage 0.016 - 0.021 cm/cm

@Thickness 3.20 mm
0.016 - 0.021 in/in

@Thickness 0.126 in
ASTM D 955
RTP Company RTP 2700 S-60A MD NATURAL Saturated Styrenic Block Copolymer ISO 10993 Tested
ISO 10993 is used to evaluate the biocompatibility of medical devices. Consult RTP Company for more details.
Linear Mold Shrinkage 0.017 - 0.021 cm/cm
0.017 - 0.021 in/in
Asahi Kasei Method
Asahi Kasei Tenac® 7054 Homopolymer Acetal Resin
High-flow grade with high crystallization rate for higher productivity.Information provided by Asahi Kasei Corporation.
Linear Mold Shrinkage 0.018 - 0.021 cm/cm
0.018 - 0.021 in/in
ASTM D955
Polymer Resources AH-GP2 Acetal Homopolymer, Medium Flow, General Purpose Molding  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Linear Mold Shrinkage 0.016 - 0.021 cm/cm

@Thickness 3.17 mm
0.016 - 0.021 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 2800B-40A FR  Thermoplastic Vulcanizate Elastomer (TPV) 40 Shore A - Flame Retardant
40 Shore A - Flame RetardantComments:40-A DurometerFlame RetardantUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information pr..
Linear Mold Shrinkage 0.016 - 0.021 cm/cm

@Thickness 3.17 mm
0.016 - 0.021 in/in

@Thickness 0.125 in
ASTM D955
RTP Company RTP 2800B-60D FR  Thermoplastic Vulcanizate Elastomer (TPV) 60 Shore D - Flame Retardant
60 Shore D - Flame RetardantComments:60-D DurometerFlame RetardantUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information pr..