Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | FRISETTA Test Method |
Nilit FRIANYL A63 HH-KV20 Nylon 6.6 for injection molding, 20% glass ball reinforced Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | With Flow; ISO 2577 |
Polykemi AB POLYform POM C M140 TF2 Polyoxymethylene, Modified Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYform POM C M90 K5 Polyoxymethylene, Mineral Reinforced Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | Across Flow; ISO 2577 |
Polykemi AB POLYshine PBT D221 PBT, Impact Modified Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | With Flow; ISO 2577 |
Polykemi AB POLYshine PBT D241 PBT, Impact Modified Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | Across Flow; ISO 2577 |
Polykemi AB SCANAMID 66 A53^E Nylon 66, Modified Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ASTM D955 |
Polymer Resources AC-GP1 Acetal Copolymer, Low Flow, High Melt Strength Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation. |
|||
Linear Mold Shrinkage | 0.018 - 0.021 cm/cm | 0.018 - 0.021 in/in | ASTM D955 |
Polymer Resources AH-GP1-[color]-H Acetal Homopolymer, Low Flow, High Melt Strength, Heat Stabilized Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | 0.125 in, DAM; ASTM D955 |
Ravago Manufacturing Americas Hylon® N2000STHL Nylon 6 (Cond) Information provided by Ravago. |
|||
Linear Mold Shrinkage | 0.018 - 0.026 cm/cm @Thickness 3.17 mm |
0.018 - 0.026 in/in @Thickness 0.125 in |
ASTM D955 |
RTP Company RTP 700 TFE 15 High Density Polyethylene (HDPE), PTFE Lubricated |
|||
Linear Mold Shrinkage | 0.018 - 0.025 cm/cm @Thickness 3.17 mm |
0.018 - 0.025 in/in @Thickness 0.125 in |
ASTM D 955 |
RTP Company RTP 799 A X 128004 D EG Low Density Polyethylene (LDPE), ESD Protection - Electrically Conductive - Extrusion Grade |
|||
Linear Mold Shrinkage | 0.018 - 0.028 cm/cm @Thickness 3.17 mm |
0.018 - 0.028 in/in @Thickness 0.125 in |
ASTM D 955 |
RTP Company RTP 799 X 50492 L Low Density Polyethylene (LDPE), Electrically Conductive |
|||
Linear Mold Shrinkage | 0.018 cm/cm @Thickness 3.17 mm |
0.018 in/in @Thickness 0.125 in |
ASTM D955 |
RTP Company RTP 800 AR 5 TFE 10 SI 2 Acetal (POM), Aramid Fiber Reinforced - PTFE & Silicone Lubricated |
|||
Linear Mold Shrinkage | 0.018 - 0.021 cm/cm | 0.018 - 0.021 in/in | ASTM D955 |
Polymer Resources AH-GP3 Acetal Homopolymer, High Flow Resin
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Linear Mold Shrinkage | 0.018 - 0.025 cm/cm | 0.018 - 0.025 in/in | |
Lehmann & Voss LUVOCOM® 80/TF/18/SI/2/BK Polyacetal-copolymer, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Linear Mold Shrinkage | 0.018 - 0.021 cm/cm | 0.018 - 0.021 in/in | ASTM D955 |
LG Chemical LUCEL VC127-LD Antistatic POM, Unreinforced, High Flow, For VCR Reels LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
Multibase Multi-Flex® TPE A 5003 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | 0.125inch wall |
Spartech PP7110 Talc Filled High Impact Copolymer Good material choice for applications where low to medium levels of impact are required and where stiffness and heat deflection properties remain criticalInformation provided by Spartech |
|||
Linear Mold Shrinkage | 0.018 - 0.026 cm/cm @Thickness 3.20 mm |
0.018 - 0.026 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
A. Schulman FORMION™ FI 395 Ionomer Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.018 cm/cm @Thickness 3.175 mm |
0.018 in/in @Thickness 0.1250 in |
ASTM D955 |
A. Schulman COMTUF® 420 Impact Modified PBT Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
Polyram RamTal PMH2017 Polyacetal Homopolymer for Injection Molding General purpose polyacetal homopolymer for injection molding applications, MFI 1.7.Information provided by Polyram. |
|||
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | |
CPT C-Flex® R70-081 Opaque Biocompatible TPE C-Flex® is a family of patented thermoplastic elastomers which range in hardness from 5 shore A to 95 shore A. C-Flex® TPE's are biocompatible polymer blends which meet or exceed the current.. |
|||
Linear Mold Shrinkage | 0.018 cm/cm | 0.018 in/in | |
Clariant Renol PA1SP0003 Nylon 66, PE Modified Reduced Coefficient of FrictionData provided by Clariant Masterbatches |
|||
Linear Mold Shrinkage | 0.018 - 0.020 cm/cm | 0.018 - 0.020 in/in | |
CPT C-Flex® R70-089 Opaque Biocompatible TPE C-Flex® is a family of patented thermoplastic elastomers which range in hardness from 5 shore A to 95 shore A. C-Flex® TPE's are biocompatible polymer blends which meet or exceed the current.. |
|||
Linear Mold Shrinkage | 0.018 cm/cm @Thickness 2.00 mm |
0.018 in/in @Thickness 0.0787 in |
ISO 294-4 |
Ascend Performance Materials Vydyne® 49 Nylon 66, DAM Vydyne® 49 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved imp.. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | Asahi Kasei Method |
Asahi Kasei Tenac® 4012 Homopolymer Acetal Resin Medium viscosity grade, with reduced stiffness and increased elongation through addition of special polymersInformation provided by Asahi Kasei Corporation. |
|||
Linear Mold Shrinkage | 0.018 cm/cm @Thickness 2.00 mm |
0.018 in/in @Thickness 0.0787 in |
ISO 294-4 |
Ascend Performance Materials Vydyne® 49 Nylon 66, Conditioned Vydyne® 49 is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved imp.. |
|||
Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ASTM D955 |
Polymer Resources AC-GP2 Acetal Copolymer, Medium Flow, General Purpose Molding
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Linear Mold Shrinkage | 0.018 - 0.028 cm/cm @Thickness 3.20 mm |
0.018 - 0.028 in/in @Thickness 0.126 in |
ASTM D 955 |
RTP Company RTP 899 X 120648 C Acetal (POM) Wear Alloy - APWA (All Polymeric Wear Additive) |