 POLYMER SEARCH

Polymer Resources ABS-FR Flame Retardant ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources ABS-FR Flame Retardant ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame Retardant Acrylonitrile Butadiene StyreneFeatures: • Flame Retardant • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 4.0 - 16 g/10 min

@Load 3.80 kg,
Temperature 230 °C
4.0 - 16 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ASTM D785
Tensile Strength at Break 37.9 MPa
5500 psi
ASTM D638
Tensile Strength, Yield 40.7 MPa
5900 psi
ASTM D638
Elongation at Break 10 %
10 %
ASTM D638
Elongation at Yield 2.2 %
2.2 %
ASTM D638
Tensile Modulus 2.28 GPa
330 ksi
ASTM D638
Flexural Strength 62.1 MPa
9000 psi
ASTM D790
Flexural Modulus 2.38 GPa
345 ksi
ASTM D790
Izod Impact, Notched 2.14 J/cm

@Temperature 22.8 °C
4.00 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Izod Impact, Notched (ISO) 6.30 kJ/m²

@Temperature -30.0 °C
3.00 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
18.9 kJ/m²

@Temperature 22.8 °C
9.00 ft-lb/in²

@Temperature 73.0 °F
ISO 180/1A
Charpy Impact, Notched 1.89 J/cm²

@Temperature 22.8 °C
9.00 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Gardner Impact 16.9 J
12.5 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 87.8 °C
190 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C
180 °F
ASTM D648
Vicat Softening Point 90.6 °C
195 °F
120°C/h, 50 N; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0 - 5VA

@Thickness 3.00 mm
V-0 - 5VA

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Rear Barrel Temperature 171 - 182 °C
340 - 360 °F
Middle Barrel Temperature 199 - 210 °C
390 - 410 °F
Front Barrel Temperature 210 - 221 °C
410 - 430 °F
Melt Temperature 204 - 232 °C
400 - 450 °F
Mold Temperature 48.9 - 71.1 °C
120 - 160 °F
Drying Temperature 82.2 - 93.3 °C
180 - 200 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.001