Overview of materials for Phenolic, Novolac, Mineral/Glass Filled

Category	Polymer , Thermoset , Phenolic , Phenolic, Novolac, Mineral/Glass Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Overview of materials for Phenolic, Novolac, Mineral/Glass Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Glass Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.

Physical Properties	Metric	English	Comments
Density	1.55 - 2.10 g/cc	0.0560 - 0.0759 lb/in³	Average value: 1.87 g/cc Grade Count:23
Water Absorption	0.0300 - 0.150 %	0.0300 - 0.150 %	Average value: 0.0842 % Grade Count:16
Linear Mold Shrinkage	0.000600 - 0.00350 cm/cm	0.000600 - 0.00350 in/in	Average value: 0.00197 cm/cm Grade Count:23

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell E	80.0 - 125	80.0 - 125	Average value: 97.9 Grade Count:13
Tensile Strength, Ultimate	31.0 - 108 MPa	4500 - 15700 psi	Average value: 74.4 MPa Grade Count:23
Elongation at Break	0.272 - 1.80 %	0.272 - 1.80 %	Average value: 0.708 % Grade Count:19
Modulus of Elasticity	9.50 - 30.0 GPa	1380 - 4350 ksi	Average value: 18.7 GPa Grade Count:19
Flexural Yield Strength	60.0 - 190 MPa	8700 - 27600 psi	Average value: 137 MPa Grade Count:23
Flexural Modulus	7.50 - 27.0 GPa	1090 - 3920 ksi	Average value: 16.7 GPa Grade Count:23
Compressive Yield Strength	156 - 410 MPa	22600 - 59500 psi	Average value: 250 MPa Grade Count:23
Poissons Ratio	0.310 - 0.330	0.310 - 0.330	Average value: 0.317 Grade Count:3
Shear Modulus	5.46 - 5.98 GPa	792 - 867 ksi	Average value: 5.76 GPa Grade Count:3
Izod Impact, Notched	0.163 - 0.450 J/cm	0.305 - 0.843 ft-lb/in	Average value: 0.363 J/cm Grade Count:12
Charpy Impact Unnotched	0.400 - 1.50 J/cm²	1.90 - 7.14 ft-lb/in²	Average value: 0.928 J/cm² Grade Count:10
Charpy Impact, Notched	0.195 - 0.550 J/cm²	0.928 - 2.62 ft-lb/in²	Average value: 0.341 J/cm² Grade Count:20

Thermal Properties	Metric	English	Comments
CTE, linear	12.0 - 30.0 µm/m-°C	6.67 - 16.7 µin/in-°F	Average value: 18.4 µm/m-°C Grade Count:14
	49.0 - 75.0 µm/m-°C @Temperature 40.0 - 130 °C	27.2 - 41.7 µin/in-°F @Temperature 104 - 266 °F	Average value: 62.0 µm/m-°C Grade Count:2
CTE, linear, Transverse to Flow	20.0 - 45.0 µm/m-°C	11.1 - 25.0 µin/in-°F	Average value: 28.7 µm/m-°C Grade Count:10
Thermal Conductivity	0.580 - 0.580 W/m-K @Temperature 100 - 100 °C	4.03 - 4.03 BTU-in/hr-ft²-°F @Temperature 212 - 212 °F	Average value: 0.580 W/m-K Grade Count:1
Maximum Service Temperature, Air	150 - 250 °C	302 - 482 °F	Average value: 211 °C Grade Count:12
Deflection Temperature at 1.8 MPa (264 psi)	170 - 282 °C	338 - 540 °F	Average value: 229 °C Grade Count:23
Deflection Temperature at 8.0 MPa	150 - 185 °C	302 - 365 °F	Average value: 166 °C Grade Count:3
Flammability, UL94	HB - V-0	HB - V-0	Grade Count:19

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.90e+11 - 1.74e+15 ohm-cm	1.90e+11 - 1.74e+15 ohm-cm	Average value: 1.77e+14 ohm-cm Grade Count:10
Insulation Resistance	1.00e+11 - 1.00e+14 ohm	1.00e+11 - 1.00e+14 ohm	Average value: 2.19e+13 ohm Grade Count:3
Dielectric Constant	4.50 - 5.60	4.50 - 5.60	Average value: 5.13 Grade Count:11
Dielectric Strength	8.60 - 35.0 kV/mm	218 - 889 kV/in	Average value: 17.7 kV/mm Grade Count:20
Dissipation Factor	0.0120 - 0.286	0.0120 - 0.286	Average value: 0.0557 Grade Count:11
Arc Resistance	48.0 - 185 sec	48.0 - 185 sec	Average value: 152 sec Grade Count:13
Comparative Tracking Index	175 - 325 V	175 - 325 V	Average value: 207 V Grade Count:17