Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Property : Deflection Temperature at 8.0 MPa = 150 °C Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Thermal Properties Metric English Comments
Deflection Temperature at 8.0 MPa 150 - 170 °C
302 - 338 °F
ISO 75-C
Raschig Group RALUPOL® 4566 UP Polyester
Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Lanxess Pocan® T 7391 POS151 000000 PBT + PET, 45% Glass Fiber  (discontinued **)
PBT+PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized
Deflection Temperature at 8.0 MPa 150 - 171 °C
302 - 340 °F
Average value: 166 °C Grade Count:3
Overview of materials for Phenolic, Novolac, Glass Filled
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Glass Filled". Each property range of values reported is minimum and maximum values o..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-2
Hexion Bakelite™ PF 2774 Phenolic Formaldehyde Resin, Dishwasher Proof, Improved Electrical Properties, Low Shrinkage, UL Listed
Phenolic molding compound, inorganically filled, glass fiber reinforced, increased dimensional stability, averaged notched impact strength, average heat resistance, improved electrical properties, U..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Lanxess Durethan® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber
PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Lanxess Pocan® DP 7244 000000 PBT, 30% Glass Fiber
PBT, 30% glass fibers, injection molding, flame retardant
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1, -2
Lanxess Pocan® T 7391 POS151 900044 PBT + PET, 45% Glass Fiber
PBT + PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load UV stabilizedInformation provided by LANXESS.
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Lanxess Durethan® BKV 30 H2.0 EF 900116 Nylon 6, 30% Glass Fiber
PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance
Deflection Temperature at 8.0 MPa 150 - 170 °C
302 - 338 °F
ISO 75 C
Vyncolit X681 Novolac Phenolic
Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica..
Deflection Temperature at 8.0 MPa 150 - 170 °C
302 - 338 °F
ISO 75 C
Vyncolit 2950 W Novolac Phenolic
Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
EMS-Grivory Grivory® LV-65H SST nat PA12-GF65
Product description: Grilamid LV-65H SST natural is a 65% glass fiber reinforced, heat stabilized engineering thermoplastic based on polyamide 12, designed for complex structural parts with the foll..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4063 black 9238 PA6T/66-GF30
Product description: Grivory XE 4063 is a 30% glass-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. This Grivory HT product is partia..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4105 black 9992 PA610-GF50
Product description: Grilamid XE 4105 black 9992 is a 50% glass fiber reinforced, heat stabilized and UV resistant polyamide 610 (PA610) injection molding grade. This product is to a large extent ba..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4105 nat PA610-GF50
Product description: Grilamid XE 4105 natural is a 50% glass fiber reinforced, heat stabilized polyamide 610 (PA610) injection molding grade. This product is to a large extent based on renewable raw..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4116 black 9288 PA1010-GF55
Product description: Grilamid XE 4116 black 9288 is a 55% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is especially suitable for the manufacturing of thin-walled, paint..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
EMS-Grivory Grivory® XE 4116 nat PA1010-GF55
Product description: Grilamid XE 4116 natural is a 55% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is especially suitable for the manufacturing of thin-walled, painted ..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-2
Hexion Bakelite™ PF 4041 Phenolic Formaldehyde Resin, Resistant to High Temperatures  (discontinued **)
Phenolic molding compound, glass fiber reinforced and inorganically filled, elasticized. Very good heat resistance, very good mechanical properties, reduced mold shrinkage and post-shrinkage, good ..
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Lanxess Durethan® BKV 35 H2.0 901510 Nylon 6, 35% Glass Fiber
PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistanceApplication Examples: automotive structures
Deflection Temperature at 8.0 MPa 150 °C
302 °F
ISO 75-1/-2
Lanxess Pocan® DP B 3235 XF 901510 PBT, 30% Glass Fiber  (discontinued **)
PBT, 30% glass fibers, injection molding, improved flowability