Polymer Property : Deflection Temperature at 8.0 MPa = 302 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75-C
Raschig Group 6551 DAIP Diallyl Phthalate (DAP), Cast, Mineral Filler Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi..
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75-C
Raschig Group EPOXIDUR® 3585 EP Epoxy, Molded, Glass Fiber Filler Glass-fiber reinforced and inorganically filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties and dimensional stability even at high temperatures, excel..
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75-C
Raschig Group RALUPOL® 4566 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u..
Deflection Temperature at 8.0 MPa	150 - 171 °C	302 - 340 °F	Average value: 166 °C Grade Count:3
Overview of materials for Phenolic, Novolac, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Glass Filled". Each property range of values reported is minimum and maximum values o..
Deflection Temperature at 8.0 MPa	150 - 185 °C	302 - 365 °F	Average value: 166 °C Grade Count:3
Overview of materials for Phenolic, Novolac, Mineral/Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Glass Filled". Each property range of values reported is minimum and maximum ..
Deflection Temperature at 8.0 MPa	150 °C	302 °F	ISO 75-2
Hexion Bakelite™ PF 2774 Phenolic Formaldehyde Resin, Dishwasher Proof, Improved Electrical Properties, Low Shrinkage, UL Listed Phenolic molding compound, inorganically filled, glass fiber reinforced, increased dimensional stability, averaged notched impact strength, average heat resistance, improved electrical properties, U..
Deflection Temperature at 8.0 MPa	150 Â°C	302 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® BKV 140 H2.0 900051 Copolyamide, 40% Glass Fiber CoPA, injection molding grade, 40% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 40, even in..
Deflection Temperature at 8.0 MPa	150 Â°C	302 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® BKV 30 EF 000000 Nylon 6, 30% Glass Fiber PA 6, injection molding grade, 30% glass fibers, low viscosity (Easy Flow)
Deflection Temperature at 8.0 MPa	150 Â°C	302 Â°F	ISO 75-1/-2
Lanxess DurethanÂ® BKV 30 H2.0 EF 901510 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, good flowability (Easy Flow), good heat-ageing resistance
Deflection Temperature at 8.0 MPa	150 Â°C	302 Â°F	ISO 75-1/-2
Lanxess PocanÂ® T 7391 000000 PBT + PET, 45% Glass Fiber PBT+PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load
Deflection Temperature at 8.0 MPa	150 Â°C	302 Â°F	ISO 75-1, -2
Lanxess PocanÂ® T 7391 POS151 900044 PBT + PET, 45% Glass Fiber PBT + PET, 45% glass fibers, injection molding, improved surface finish, increased temperature peak load UV stabilizedInformation provided by LANXESS.
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75 C
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica..
Deflection Temperature at 8.0 MPa	150 - 170 °C	302 - 338 °F	ISO 75 C
Vyncolit 2950 W Novolac Phenolic Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group
Deflection Temperature at 8.0 MPa	150 °C	302 °F	ISO 75-1/-2
EMS-Grivory Grivory® XE 4063 black 9238 PA6T/66-GF30 Product description: Grivory XE 4063 is a 30% glass-fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. This Grivory HT product is partia..
Deflection Temperature at 8.0 MPa	150 °C	302 °F	ISO 75-1/-2
EMS-Grivory Grivory® XE 4105 black 9992 PA610-GF50 Product description: Grilamid XE 4105 black 9992 is a 50% glass fiber reinforced, heat stabilized and UV resistant polyamide 610 (PA610) injection molding grade. This product is to a large extent ba..
Deflection Temperature at 8.0 MPa	150 °C	302 °F	ISO 75-1/-2
EMS-Grivory Grivory® XE 4116 black 9288 PA1010-GF55 Product description: Grilamid XE 4116 black 9288 is a 55% glass fiber reinforced Polyamide 1010 injection molding grade. This grade is especially suitable for the manufacturing of thin-walled, paint..
Deflection Temperature at 8.0 MPa	150 °C	302 °F	HDT/C; ISO 75-2
Akro-Plastic Akromid® B3 GF 30 (2472) PA 6 Dry, 30% Glass Filled AKROMID® B (Polyamide 6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperatur..
Deflection Temperature at 8.0 MPa	150 °C	302 °F	ISO 75-1/-2
Lanxess Durethan® BKV 35 H2.0 901510 Nylon 6, 35% Glass Fiber PA 6, injection molding grade, 35% glass fibers, good heat-ageing resistanceApplication Examples: automotive structures
Deflection Temperature at 8.0 MPa	150 °C	302 °F	ISO 75-1/-2
Lanxess Pocan® DP B 3235 XF 901510 PBT, 30% Glass Fiber (discontinued **) PBT, 30% glass fibers, injection molding, improved flowability