Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |
Plastcom SLOVAMID 66 T 36 TS PA66, 36% mineral filling FeaturesPA 66 with the content of 36 % chemically modified mineral filling. Used for holders of electric hand tools, for hobby tools, gears, covers of electric tools, flat products, automobile wheel.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | 120°C/h; ISO 75/1 |
Polykemi AB SCANMID 6 B43^ D F15 Nylon 6, Glass Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | Injection and Compression; ISO 75-A |
Raschig Group MELOPLAS® 2500 MF Cellulose-reinforced MF molding compound in white and colored shades. Very good electrical properties, high surface hardness, good abrasion- and UV-stability, very good resistance to chemicals - al.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | DAM; ISO 75-1/-2 |
DuPont Performance Polymers Minlon® 10B140 BK061 Nylon 66
(Unverified Data**) Minlon® 10B140 BK061 is a 40% mineral reinforced, black polyamide 66 resin for injection molding. It has very low warpage.Information provided by DuPont Performance Polymers |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1, -2 |
Lanxess Durethan® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified PA 6, 15% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75/Af |
Solvay TECHNYL® C 52G1 V25 Grey R7035 (XC 1329/A) PA6, DRY Description: Polyamide 6, Glass-filled, glow-wire modified, color stabilized, lubricated for injection molding.Available in: Asia Pacific, Europe, Latin America and North America Product Application.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
SABIC Innovative Plastics Valox® VX5121 PBT (Europe-Africa-Middle East) VALOX VX5121 is a 15 % glass reinforced PBT+PC blend with low warpage characteristics.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C @Thickness 6.40 mm |
338 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics NORYL GTX GTX9400W PPE+PS+PA High flow PPO+PA. Power distribution box applications. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics Valox® SHF4930 PBT Super high flow FR PBT grade with 15% Glass reinforced |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C @Thickness 3.20 mm |
338 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP YF005 TPEE (Asia Pacific) LNP* Thermocomp* YF005 is a compound based on TPEE resin containing Glass Fiber. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af |
Vyncolit 2923 W Novolac Phenolic Mineral filled phenolic molding compound with excellent heat resistance and dimensional stability.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af |
Vyncolit X681 Novolac Phenolic Glass fiber filled phenolic molding compound with excellent mechanical properties and a low coefficient of friction. Tribological compound with PTFE additive.USES: Water pump seals and self-lubrica.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 |
Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized 15% Glass fiber reinforced, impact modified and UV stabilized Nylon 6 for injection molding applications.Information provided by Polyram. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af |
Vyncolit 2950 W Novolac Phenolic Mineral and glass fiber filled phenolic molding compound with a very high strain to failure in flexure. UL listed.USES: Armature insulation.Information provided by Vyncolit, a Sumitomo Bak Group |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 179 |
CP-Polymer-Technik Wellamid® 6000/52 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Low Temperature Impact Modified, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 179 |
CP-Polymer-Technik Wellamid® 6000/58 GV 15 HWUVCP 15% Glass Fiber Nylon 6, Impact Modified Until -40°C, UV Stabilized, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LV-65H FWA nat PA12-GF65 Product description: Grilamid LV-65H FWA natural is a 65 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
DuPont Performance Polymers Crastin® LW9030 BK851 PBT+ASA
(Unverified Data**) 30% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9030 BK851 is a 30% glass fiber reinforced black polybutylene terephthalate blend for injection mol.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
Eurostar Starflam AFR682B1 PA66, Mineral Reinforced, Flame Retardant, Injection Molding Starflam AFR682B1 is a Flame Retardant, Mineral Filled Polyamide 66, Injection Molding ResinInformation provided by Eurostar. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
EMS-Grivory Grivory® LCL-3 H anthracite PA12-CF30 Product description: Grilamid LCL-3H anthracite is based on a heat stabilized PA12 and 30% long carbon fibers. Grilamid LCL-3H anthracite is characterized by the following key-properties: high stiff.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |
Arkema Group Rilsan® BZM 23 G9 Nylon 11, 23% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA11,MS,18-040,(G+C)(F+D)(25+05)Rigid grade with glass fiber (23%) and graphite filler for injection molding. Available color: steel black gray. Additive free.Rigidity. Low fric.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 |
BASF Ultramid® 8272G HS BK-102 12% Glass Filled PA6 (Dry) Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, nylon 6 blow molding compound offering an excellent balance of engineering properties combined with the.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
BASF Ultramid® B3UG4 BK 23215 20% Glass Filled PA66 FR (Dry) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ASTM D648 |
Beijing Chemical Industry KAIFA® HN201-G10 PA6 Resin 10% glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
BASF Ultramid® B3UG4 LS BK 23215 20% Glass Filled PA66 FR (Dry) Description: Halogen-free and phosphorus free flame retardant injection-molding grade with outstanding free-flow properties, good electrical properties and low smoke density; resistant to glow wire.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 |
DuPont Performance Polymers Crastin® LW9030 BK851 PBT
(Unverified Data**) Crastin® LW9030 BK851 is a 30% glass fiber reinforced, black polybutylene terephthalate alloy for injection molding. It has improved surface aesthetics, excellent dimensional stability and low warp.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics Valox® VX4915 ASA+PBT (Europe-Africa-Middle East) 15% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |
LATI Latilub 95-15T PSU, PTFE Filled Self-lubricating product based on Polysulfone (PSU). PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici .. |