Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours

Category Metal , Superalloy , Iron Base
Manufacturer Haynes International, Inc.
Trade Name Multimet®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and is readily fabricated. Current applications include aircraft, including tailpipes and tailcones, afterburner parts, exhaust manifolds, combustion chambers, turbine blades, buckets and nozzles. Excellent service for high temperature bolts.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.20 g/cc
0.296 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 675 MPa
97900 psi
103 MPa

@Temperature 1066 °C
 14900 psi

@Temperature 1951 °F
150 MPa

@Temperature 982 °C
 21800 psi

@Temperature 1800 °F
230 MPa

@Temperature 899 °C
 33400 psi

@Temperature 1650 °F
321 MPa

@Temperature 816 °C
 46600 psi

@Temperature 1500 °F
380 MPa

@Temperature 732 °C
 55100 psi

@Temperature 1350 °F
446 MPa

@Temperature 649 °C
 64700 psi

@Temperature 1200 °F
451 MPa

@Temperature 593 °C
 65400 psi

@Temperature 1100 °F
487 MPa

@Temperature 538 °C
 70600 psi

@Temperature 1000 °F
530 MPa

@Temperature 427 °C
 76900 psi

@Temperature 801 °F
538 MPa

@Temperature 316 °C
 78000 psi

@Temperature 601 °F
549 MPa

@Temperature 204 °C
 79600 psi

@Temperature 399 °F
Tensile Strength, Yield 372 MPa

@Strain 0.200 %
 54000 psi

@Strain 0.200 %
Elongation at Break 23 %
23 %
in 50.8 mm
11 %

@Temperature 816 °C
 11 %

@Temperature 1500 °F
 in 50.8 mm
15 %

@Temperature 732 °C
 15 %

@Temperature 1350 °F
 in 50.8 mm
23 %

@Temperature 593 °C
 23 %

@Temperature 1100 °F
 in 50.8 mm
23 %

@Temperature 649 °C
 23 %

@Temperature 1200 °F
 in 50.8 mm
23 %

@Temperature 204 °C
 23 %

@Temperature 399 °F
 in 50.8 mm
24 %

@Temperature 316 °C
 24 %

@Temperature 601 °F
 in 50.8 mm
24 %

@Temperature 899 °C
 24 %

@Temperature 1650 °F
 in 50.8 mm
25 %

@Temperature 427 °C
 25 %

@Temperature 801 °F
 in 50.8 mm
25 %

@Temperature 538 °C
 25 %

@Temperature 1000 °F
 in 50.8 mm
31 %

@Temperature 982 °C
 31 %

@Temperature 1800 °F
 in 50.8 mm
39 %

@Temperature 1066 °C
 39 %

@Temperature 1951 °F
 in 50.8 mm
Reduction of Area 25 %
25 %
19 %

@Temperature 816 °C
 19 %

@Temperature 1500 °F
20 %

@Temperature 732 °C
 20 %

@Temperature 1350 °F
24 %

@Temperature 649 °C
 24 %

@Temperature 1200 °F
25 %

@Temperature 593 °C
 25 %

@Temperature 1100 °F
26 %

@Temperature 427 °C
 26 %

@Temperature 801 °F
27 %

@Temperature 538 °C
 27 %

@Temperature 1000 °F
27 %

@Temperature 204 °C
 27 %

@Temperature 399 °F
27 %

@Temperature 316 °C
 27 %

@Temperature 601 °F
29 %

@Temperature 899 °C
 29 %

@Temperature 1650 °F
42 %

@Temperature 982 °C
 42 %

@Temperature 1800 °F
45 %

@Temperature 1066 °C
 45 %

@Temperature 1951 °F
Poissons Ratio 0.298
0.298
RT
0.315

@Temperature 426 °C
 0.315

@Temperature 799 °F
0.319

@Temperature -78.0 °C
 0.319

@Temperature -108 °F
0.325

@Temperature 650 °C
 0.325

@Temperature 1200 °F
0.339

@Temperature 816 °C
 0.339

@Temperature 1500 °F
Thermal Properties Metric English Comments
CTE, linear 15.3 µm/m-°C

@Temperature 23.0 - 300 °C
 8.50 µin/in-°F

@Temperature 73.4 - 572 °F
15.6 µm/m-°C

@Temperature 23.0 - 400 °C
 8.67 µin/in-°F

@Temperature 73.4 - 752 °F
16.0 µm/m-°C

@Temperature 23.0 - 500 °C
 8.89 µin/in-°F

@Temperature 73.4 - 932 °F
16.7 µm/m-°C

@Temperature 23.0 - 600 °C
 9.28 µin/in-°F

@Temperature 73.4 - 1110 °F
17.2 µm/m-°C

@Temperature 23.0 - 700 °C
 9.56 µin/in-°F

@Temperature 73.4 - 1290 °F
17.5 µm/m-°C

@Temperature 23.0 - 800 °C
 9.72 µin/in-°F

@Temperature 73.4 - 1470 °F
17.8 µm/m-°C

@Temperature 23.0 - 900 °C
 9.89 µin/in-°F

@Temperature 73.4 - 1650 °F
17.8 µm/m-°C

@Temperature 23.0 - 1000 °C
 9.89 µin/in-°F

@Temperature 73.4 - 1830 °F
18.4 µm/m-°C

@Temperature 23.0 - 1100 °C
 10.2 µin/in-°F

@Temperature 73.4 - 2010 °F
Specific Heat Capacity 0.435 J/g-°C

@Temperature >=100 °C
 0.104 BTU/lb-°F

@Temperature >=212 °F
Thermal Conductivity 15.9 W/m-K

@Temperature 300 °C
 110 BTU-in/hr-ft²-°F

@Temperature 572 °F
17.3 W/m-K

@Temperature 400 °C
 120 BTU-in/hr-ft²-°F

@Temperature 752 °F
18.6 W/m-K

@Temperature 500 °C
 129 BTU-in/hr-ft²-°F

@Temperature 932 °F
20.0 W/m-K

@Temperature 600 °C
 139 BTU-in/hr-ft²-°F

@Temperature 1110 °F
20.0 W/m-K

@Temperature 200 °C
 139 BTU-in/hr-ft²-°F

@Temperature 392 °F
Melting Point 1288 - 1354 °C
2350 - 2469 °F
Solidus 1288 °C
2350 °F
Liquidus 1354 °C
2469 °F
Optical Properties Metric English Comments
Emissivity (0-1) 0.88

@Temperature 1090 °C
 0.88

@Temperature 1990 °F
 Oxidized
Component Elements Properties Metric English Comments
Carbon, C 0.080 - 0.16 %
0.080 - 0.16 %
Cb + Ta 0.75 - 1.25 %
0.75 - 1.25 %
Chromium, Cr 20 - 22.5 %
20 - 22.5 %
Cobalt, Co 18.5 - 21 %
18.5 - 21 %
Iron, Fe 33 %
33 %
As remainder
Manganese, Mn 1.0 - 2.0 %
1.0 - 2.0 %
Molybdenum, Mo 2.5 - 3.5 %
2.5 - 3.5 %
Nickel, Ni 19 - 21 %
19 - 21 %
Nitrogen, N 0.10 - 0.20 %
0.10 - 0.20 %
Silicon, Si <= 1.0 %
<= 1.0 %
Tungsten, W 2.0 - 3.0 %
2.0 - 3.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000930 ohm-cm

@Temperature 22.0 °C
 0.0000930 ohm-cm

@Temperature 71.6 °F