Polymer Property : CTE, linear = 9.89 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.8 µm/m-°C @Temperature 25.0 - 1000 °C |
9.89 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 25.0 - 1000 °C |
9.89 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 25.0 - 1000 °C |
9.89 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 20.0 - 1000 °C |
9.89 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Waspaloy™ alloy, sheet Age-hardenable superalloy with very good strength at temperatures up 980°C (1800°F), can be cold-formed in the annealed condition, may also be hot formed at 1040°C (1900°F) and above, go.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 25.0 - 1000 °C |
9.89 µin/in-°F @Temperature 77.0 - 1830 °F |
|
| Haynes HR-120® alloy, solution heat-treated plate Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 900 °C |
9.89 µin/in-°F @Temperature 73.4 - 1650 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 17.8 µm/m-°C @Temperature 23.0 - 1000 °C |
9.89 µin/in-°F @Temperature 73.4 - 1830 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||