- Polymer Property : CTE, linear = 18.4 µm/m-°C
Polymer Property : CTE, linear = 18.4 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.4 µm/m-°C @Temperature 500 °C |
10.2 µin/in-°F @Temperature 932 °F |
|
| Outokumpu 4828 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 500 °C |
10.2 µin/in-°F @Temperature 932 °F |
|
| Outokumpu 4833 High Temperature Austenitic Stainless Steel Standardized high temperature steel for service at temperatures of up to 950-1000°C in dry air. Utilization in the temperature range of 600-900°C can lead to embrittlement.Applications: Heat and .. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 500 °C |
10.2 µin/in-°F @Temperature 932 °F |
|
| Outokumpu 4845 High Temperature Austenitic Stainless Steel Standardized high-temperature steel for use at temperatures up to 1100°C in dry air. Prone to embrittlement after exposure between 600-900°C. Applications: Heat and creep resistance. For use o.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 500 °C |
10.2 µin/in-°F @Temperature 932 °F |
|
| Outokumpu 4878 High Temperature Austenitic Stainless Steel Heat-resistant variant of 1.4541, with a slightly higher max carbon content. Recommended max service temperature for this steel in dry air is 800°C. Applications: Heat and creep resistance. For .. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, GTAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature -30.0 - 70.0 °C |
10.2 µin/in-°F @Temperature -22.0 - 158 °F |
|
| Schott LITHOTEC-CAF2 Glass Information Provided by SCHOTT North America, Inc. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 500 °C |
10.2 µin/in-°F @Temperature 932 °F |
|
| Outokumpu 4948 High Temperature Austenitic Stainless Steel Creep-resistant variant of 1.4301, with a standardized minimum carbon content for service at temperatures of up to 800°C in dry air.Applications: Heat and creep resistance. For use over 550°C for.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 18.4 µm/m-°C @Temperature 23.0 - 1100 °C |
10.2 µin/in-°F @Temperature 73.4 - 2010 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||