Polymer Property : Thermal Conductivity = 17.3 W/m-K Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 1.32 mm thick sheet, 1177Â°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 1.6 mm thick sheet, 1177Â°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 12.7 mm (1/2 in.) thick plate, 1185Â°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 25.4-50.8 mm forged bar, 1185Â°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 1185Â°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, GTAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, sand cast, 1171Â°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 400 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 752 Â°F
Haynes MultimetÂ® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Thermal Conductivity	17.3 W/m-K @Temperature 500 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
HP Alloys Alloy B-2, Solution Treated, 10% Cold Worked Solution Treated, 10% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Thermal Conductivity	17.3 W/m-K @Temperature 500 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
HP Alloys Alloy B-2, Solution Treated, 20% Cold Worked Solution Treated, 20% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Thermal Conductivity	17.3 W/m-K @Temperature 500 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
HP Alloys Alloy B-2, Solution Treated, 30% Cold Worked Solution Treated, 30% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Thermal Conductivity	17.3 W/m-K @Temperature 500 Â°C	120 BTU-in/hr-ftÂ²-Â°F @Temperature 932 Â°F
HP Alloys Alloy B-2, Solution Treated, 40% Cold Worked Solution Treated, 40% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.
Thermal Conductivity	17.3 W/m-K @Temperature 400 °C	120 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Thermal Conductivity	17.3 W/m-K @Temperature 400 °C	120 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Thermal Conductivity	17.3 W/m-K @Temperature 400 °C	120 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Thermal Conductivity	17.3 W/m-K @Temperature 400 °C	120 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Thermal Conductivity	17.3 W/m-K @Temperature 400 °C	120 BTU-in/hr-ft²-°F @Temperature 752 °F
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i..
Thermal Conductivity	17.3 W/m-K @Temperature 500 °C	120 BTU-in/hr-ft²-°F @Temperature 932 °F
HP Alloys Alloy B-2, Solution Treated, 50% Cold Worked Solution Treated, 50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc. and Haynes International.