Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polycasa COPOL PETG

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer Polycasa
Trade Name COPOL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polycasa COPOL PETG.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
QUINN COPOL has good optical properties, brilliant surface, easy to vacuum form without pre-drying, low water absorption, very good chemical resistance, and high impact properties.Bus shelters (UV-version)Poster glazingMachine guardsMedical appliance packagingDisplaysRefrigerators and cold storeroom equipmentLenticular lenses / Graphic ArtsLighting controllers for hazardous areasQuinn Manufacturing Group rebranded its Plastics Division as Polycasa in 2013.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ISO 527-2
Elongation at Break 14 %
14 %
ISO 527-2
Tensile Modulus 2.40 GPa
348 ksi
ISO 527-2
Flexural Strength 85.0 MPa
12300 psi
ISO 178
Flexural Modulus 2.35 GPa
341 ksi
ISO 178
Charpy Impact Unnotched NB
NB
ISO 179-1
Charpy Impact, Notched 0.153 J/cm²
0.728 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear 59.0 µm/m-°C

@Temperature 20.0 °C
32.8 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Thermal Conductivity 0.162 W/m-K
1.12 BTU-in/hr-ft²-°F
DIN 52612
Maximum Service Temperature, Air 69.0 °C
156 °F
Deflection Temperature at 0.46 MPa (66 psi) 69.0 °C
156 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
ISO 75-2
Vicat Softening Point 78.0 °C
172 °F
ISO 306
Decomposition Temperature >= 280 °C
>= 536 °F
Optical Properties Metric English Comments
Haze <= 1.1 %
<= 1.1 %
Transmission, Visible 87 %
87 %
DIN 5036-3
Electrical Properties Metric English Comments
Volume Resistivity 6.05e+14 ohm-cm
6.05e+14 ohm-cm
IEC 93
Surface Resistance 6.62e+14 ohm
6.62e+14 ohm
IEC 93
Dielectric Constant 3.3

@Frequency 1000 Hz
3.3

@Frequency 1000 Hz
Dielectric Strength 10.7 kV/mm
272 kV/in
IEC 60243
Dissipation Factor 0.020

@Frequency 50 Hz
0.020

@Frequency 50 Hz
IEC 250
Processing Properties Metric English Comments
Processing Temperature 120 - 160 °C
248 - 320 °F
Sheet Forming