- Polymer Property : CTE, linear = 9.72 µin/in-°F
Polymer Property : CTE, linear = 9.72 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4303 Cr-Ni Austenitic Stainless Steel Good corrosion resistance with excellent drawing properties.Applications: Suitable for cold formed components where good workability is required. Fasteners, studs.Available in hot rolled plate (Qua.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4372 Cr-Ni Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, and rod forms. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4406 Cr-Ni-Mo Austenitic Stainless Steel Applications: Wet corrosion resistance and general service.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 400 °C |
9.72 µin/in-°F @Temperature 752 °F |
|
| Outokumpu 4438 High Performance Austenitic Stainless Steel Very good corrosion resistance, weldable, and resistant to sensitization.Available in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar,.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.72 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Industeel CLC 17.12.2 Ti Titanium Stabilized 18Cr-11Ni-2Mo Austenitic Stainless Steel CLC 17-12-2Ti is a Titanium stabilized austenitic stainless steel. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform and localized co.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 20.0 - 200 °C |
9.72 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Industeel NUCL 18.10 B4 Natural Boron (Min 1% wt) Alloyed 304 Stainless Steel Description: Isotope B10 has the property to capture neutrons produced by nuclear reactions. Natural boron contains about 19.9 at% or 18.45 wt % of B10 isotope, the remaining being B11 isotope. NUCL.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 23.0 - 800 °C |
9.72 µin/in-°F @Temperature 73.4 - 1470 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 17.5 µm/m-°C @Temperature 20.0 - 500 °C |
9.72 µin/in-°F @Temperature 68.0 - 932 °F |
|
| Industeel UREA 25.22.2 Plants Description: CLI UREA 25.22.2 chemical composition has been optimized for specific uses in Urea plants. It is a 310L modified austenitic stainless steel with low carbon, low silicon and high nitroge.. |
|||