Polymer Property : Tensile Strength, Ultimate = 14900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
PolyOne Lubri-Tech™ PS-30GF/ 02S PBT Polyester - 30% Glass Fiber - 2% Silicone (discontinued **) Data provided by PolyOne.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
PolyOne Stat-Tech™ PI-10SS/000 Polyetherimide - 10% Stainless Steel Fiber (discontinued **) Data provided by PolyOne.
Tensile Strength, Ultimate	103 MPa	14900 psi
Cookson Group Plaskon® 3100 Novolac Epoxy Molding Compound (discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A flame retardant, novolac-hardened epoxy molding compound recommended for semiconductor packages that are not stress sensitive.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Glastic Laminates/Shapes Polyester, Channels and Structural Shapes (GPO3) Data provided by Glastic Corporation.NEMA GPO-3. Average data - may vary with the size and shape of the electrical insulating structural product.
Tensile Strength, Ultimate	103 MPa @Temperature 1066 Â°C	14900 psi @Temperature 1951 Â°F
Haynes MultimetÂ® alloy, sand cast, 1171Â°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Ultimate	103 MPa	14900 psi
Haysite 42100 Polyester SMC, 22% Glass Reinforced Haysite Grade 42100 is a fiber glass reinforced thermoset polyester sheet molding compound exhibiting excellent moldability. It is designed for compression molded parts requiring high strength and g..
Tensile Strength, Ultimate	103 MPa	14900 psi
Haysite 44500 Vinyl Ester SMC, 30% Glass Reinforced The 44500 series sheet molding compound offers high strength and excellent resistance to corrosive agents. This compression molding grade is formulated with a vinyl ester resin system.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Sumitomo Bakelite DurezÂ® 23570 Phenolic, Injection Grade Durez 23570 Black Phenolic is a glass and mineral filled two-stage, special purpose molding material. It is designed for high strength, good dimensional stability, and electrical properties even aft..
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Sumitomo Bakelite DurezÂ® 32633 Glass Filled Phenolic, Compression Grade Durez 32633 Black Phenolic is a two-stage, glass filled, special purpose molding compound. It is designed for applications requiring high physical strengths, dimensional stability, and heat resista..
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Sumitomo Bakelite SumikonÂ® PM-6430 Glass-Filled Phenolic, Injection Grade SumikonÂ PM-6430 black Phenolic is a two stage glass fiber and mineral filled special purpose molding compound. It is especially designed for applications requiring high strength and dimensional s..
Tensile Strength, Ultimate	103 MPa	14900 psi	ISO 527-1, 2
Polyplastics Duranex® 7390W Polybutylene Terephthalate (PBT), Super low warpage, GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	103 MPa	14900 psi	ISO 527-1, 2
Polyplastics FR-PET® C3015FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose Information provided by PolyPlastics.
Tensile Strength, Ultimate	103 MPa	14900 psi	ISO 527-1, 2
Polyplastics Duranex® CN5315 Polybutylene Terephthalate (PBT), Higher gloss, Better surface appearance, 15% GF filled DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate	103 MPa	14900 psi	ISO 527-1, 2
Polyplastics FR-PET® B3015FA Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose Information provided by PolyPlastics.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638/D412
Covestro Baydur® STR/C-405 IMR Polyurethane Composite SRIM Foam, 45% Glass Filled, MDI-based 2-Component Liquid System Contains continuous strand fiberglass mat.0.118 in. thickness.Information provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer ..
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Covestro Makrolon® 8325 Polycarbonate High viscosity injection molding and extrusion grade with 20% standard glass fibers and easy mold release, high strength and stiffness.Information provided by Bayer.As of 1 September 2015, Bayer Mat..
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, Dry As Molded Low density, high rigidity, high heat distortion temperature, high retention of mechanical properties under humid conditions, flame retardant, recyclable and environmentally friendly, less glass fib..
Tensile Strength, Ultimate	103 MPa	14900 psi
Cytec Thornel® Graphite Cloth Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature..
Tensile Strength, Ultimate	103 MPa	14900 psi
Cytec Thornel® Graphite Cloth Laminate with Mil R-9299 Resin Data provided by the manufacturer, Amoco Performance Products, Inc.Carbon and graphite cloths, consisting entirely of flexible filaments, are produced by pyrolysis of rayon cloth at high temperature..
Tensile Strength, Ultimate	103 MPa	14900 psi
CMW® D54 Silver Cadmium Oxide Contact Material ASTM B781, Table 2, Type B For electrical contacts; especially resistant to welding and high surge currentsInformation provided by CMW Inc.
Tensile Strength, Ultimate	103 MPa	14900 psi	ATSM D638
Ashley Polymers Ashlene® 527-43G Nylon 66, 43% Glass Reinforced A 43% glass reinforced impact modified Nylon 66.Data provided by the manufacturer
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 415 Polyester - PBT, Glass Reinforced Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
A. Schulman ComAlloy Voloy® 417 Polyester - PBT, Glass/Mineral Reinforced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.43% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Adell BT-14 Nylon 6, 20% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
Adell BT-34 Nylon 6, 20% Glass Reinforced; Impact Modified Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
A. Schulman ComAlloy Hiloy® 263 Glass Reinforced, Modified SMA Data provided by the manufacturer, ComAlloy International Company.35% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate	103 MPa @Temperature 90.0 °C	14900 psi @Temperature 194 °F	ISO 527
LATI LASULF G/30 30% Glass Reinforced Polysulfone (PSU) (Unverified Data**) Description: Lasulf products are composed of polysulfone (PSU). They feature good thermal and mechanical properties such as excellent toughness, even at low temperatures, excellent dimensional stabi..
Tensile Strength, Ultimate	103 - 186 MPa	14900 - 27000 psi
Cosmic Plastics CP7312 Epoxy Molding Compound Data provided by the manufacturer.
Tensile Strength, Ultimate	103 MPa	14900 psi	ASTM D638
PolyOne Lubri-Tech™ MP-30GF/15T Modified PPO - 30% Glass Fiber - 15% PTFE (discontinued **) Data provided by PolyOne.