Polymer Property : CTE, linear = 16.7 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.7 µm/m-°C @Temperature 100 °C |
9.28 µin/in-°F @Temperature 212 °F |
|
| Outokumpu 4567 Austenitic Stainless Steel Good corrosion resistance with excellent low cold work hardening properties.Applications: Suitable for manufacture of cold headed fasteners.Bar and rod forms. |
|||
| CTE, linear | 16.7 - 17.7 µm/m-°C @Temperature 20.0 - 100 °C |
9.28 - 9.83 µin/in-°F @Temperature 68.0 - 212 °F |
|
| PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition F Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 0% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, 40% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, bar after 16000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, bar, after 1000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 800 °C |
9.28 µin/in-°F @Temperature 77.0 - 1470 °F |
|
| Haynes 556® alloy, sheet after 1000 hours at 648°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 21.1 - 982 °C |
9.30 µin/in-°F @Temperature 70.0 - 1800 °F |
|
| Carlson C 600 Nickel-Chromium-Iron Alloy Carlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excellent resistance to c.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 21.1 - 982 °C |
9.30 µin/in-°F @Temperature 70.0 - 1800 °F |
|
| Carlson C 600ESR Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 600 is nickel-chromium alloy, developed for use in severely corrosive environments at elevated temperatures. The high nickel content of this alloy provides excell.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 23.0 - 600 °C |
9.28 µin/in-°F @Temperature 73.4 - 1110 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 16.7 µm/m-°C @Temperature 25.0 - 900 °C |
9.28 µin/in-°F @Temperature 77.0 - 1650 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||