- Polymer Property : Solidus = 1288 °C
Polymer Property : Solidus = 1288 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, GTAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Special Metals INCONEL® alloy 740 Precipitation-Hardenable Ni-Cr-Co Superalloy INCONEL® alloy 740 is a nickel-chromium-cobalt alloy developed by Special Metals Corporation. The alloy is age hardenable by the precipitation of a gamma prime second phase. Potential applicati.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| Solidus | 1288 °C | 2350 °F | |
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||