Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 140 °C |
8.89 µin/in-°F @Temperature 32.0 - 284 °F |
X-, Y-Direction; ASTM D3386 |
Rogers Corporation TMM® TMM4 Ceramic Thermoset Polymer Composite TMM® Thermoset microwave materials are ceramic thermoset polymer composites designed for high plate-thru-hole reliability stripline and microstrip applications. The electrical and mechanical prope.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
Industeel CLC 17.12.2 L 2% Mo Containing 18 Cr –10 Ni Austenitic Stainless Steel Description: CLC 17-12-2L is one of the basic grade of the stainless steels range. 2% Molybdenum bearing ensures better corrosion resistance than CLC 18-9 L grade, particularly regarding to uniform .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
Industeel CLC 18.10 Nb Niobium Stabilized 18Cr-10Ni Austenitic Stainless Steel CLC 18-10Nb is a 18Cr-10Ni austenitic stainless steel stabilized with specific Nb addition. This kind of steel is one of the basic grades of the stainless steels range. Niobium bearing and its low c.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
Industeel CLC 18.10Ti Titanium-Stabilized 18Cr-10Ni Austenitic Stainless Steel CLC 18-10Ti is a 18Cr-9Ni austenitic stainless steel stabilized with some Titanium additions. This is a basic grades in the stainless steel range. Titanium bearing (carbide forming element) avoids i.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 400 °C |
8.89 µin/in-°F @Temperature 68.0 - 752 °F |
|
Industeel SIRIUS 309 23% Cr - 13% Ni Heat Resistant Stainless Steel Description: CLI SIRIUS 309 grade is a fully austenitic stainless steel containing 23% Cr, and 13% Ni additions. The alloy is well known for its multi-purpose high temperature corrosion resistance b.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
Industeel SIRIUS S12 20% Cr - 1.8% Si Heat Resistant Steel Description: CLI SIRIUS S12 grade is an austenitic stainless steel containing 20% Cr, 1.8 % Si and 12% Ni. The low nickel content combined with high chromium and high silicon contents provide good r.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 1093 °C |
8.89 µin/in-°F @Temperature 68.0 - 1999 °F |
|
Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 1093 °C |
8.89 µin/in-°F @Temperature 68.0 - 1999 °F |
|
Haynes Hastelloy® S alloy, gas tungsten arc welded Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Application.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 0% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 40% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 50% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 0 Annealed, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1C H14 4/4 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP4 H15 Spring, Drawn Copper Alloy Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP1 H11 1/4 hard, Rolled Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 300 °C |
8.89 µin/in-°F @Temperature 32.0 - 572 °F |
|
CLAL-MSX ARCAP Anticorrosion AP4 0 Annealed, Drawn Copper Alloy Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 760 °C |
8.89 µin/in-°F @Temperature 86.0 - 1400 °F |
|
Haynes Hastelloy® G-30® alloy, 0.71 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 1093 °C |
8.89 µin/in-°F @Temperature 68.0 - 1999 °F |
|
Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 4000 hours Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications .. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 23.0 - 500 °C |
8.89 µin/in-°F @Temperature 73.4 - 932 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.89 µin/in-°F @Temperature 68.0 - 212 °F |
|
Industeel CLC 18.9 L General Purpose 18Cr-9Ni Austenitic Stainless Steel Description: CLC 18-9L is a 18Cr-9Ni austenitic stainless steel. The grade contains small amount of ferrite (~ 3%) after solution annealing (1000-1100°C – 1832-2012°F) and water quenching. This k.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 25.0 - 800 °C |
8.89 µin/in-°F @Temperature 77.0 - 1470 °F |
|
Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 760 °C |
8.89 µin/in-°F @Temperature 86.0 - 1400 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
CTE, linear | 16.0 µm/m-°C @Temperature 30.0 - 649 °C |
8.89 µin/in-°F @Temperature 86.0 - 1200 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |