Polymer Property : Tensile Strength, Ultimate = 230 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	230 MPa @Temperature 899 Â°C	33400 psi @Temperature 1650 Â°F
Haynes MultimetÂ® alloy, sand cast, 1171Â°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816Â°C (1500Â°F), and moderate stresses up to 1093Â°C (2000Â°F). Excellent oxidation resistance, good ductilit..
Tensile Strength, Ultimate	230 MPa	33400 psi	ASTM E8
M Cubed Technologies ASC-701 Aluminum alloy-70% SiC Metal Matrix Composite High stiffness, low density, low CTE composite. Components can be formed with complicated features, and can be machined to tight tolerances. Applications in high-precision equipment--semiconductor..
Tensile Strength, Ultimate	230 MPa	33400 psi	dry; ISO 527-1/-2
DSM Novamid® 1015G50 NA/BK37 PA6-GF50 50% Glass Reinforced, Injection Molding
Tensile Strength, Ultimate	230 MPa	33400 psi	dry; ISO 527-1/-2
DSM Stanyl® TE200F8 PA46-GF40 40% Glass Reinforced, Heat Stabilized, for E&E applications
Tensile Strength, Ultimate	230 - 250 MPa	33400 - 36300 psi
AMT AM-Lite® Die Casting Magnesium Alloy AM-lite is a high surface finish die casting alloy suitable for applications that currently utilize zinc, aluminum or magnesium (alloy AZ91D) die castings, or plastic injection moldings. AM-lite has..
Tensile Strength, Ultimate	230 MPa	33400 psi	Same value from ASTM and ISO tests; 5 mm/min.
BASF Capron® 8234G 44% Glass-Filled Nylon 6 (Dry) (discontinued **) Capron 8234G is a 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. It is ..
Tensile Strength, Ultimate	230 MPa	33400 psi	dry; ISO 527-1/-2
DSM Novamid® 3010CF30 BK PA66-CF30 30% Carbon Reinforced