- Polymer Property : CTE, linear = 15.3 µm/m-°C
Polymer Property : CTE, linear = 15.3 µm/m-°C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.3 - 16.3 µm/m-°C @Temperature 20.0 - 100 °C |
8.50 - 9.06 µin/in-°F @Temperature 68.0 - 212 °F |
|
| PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T6 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 15.3 - 16.3 µm/m-°C @Temperature 20.0 - 100 °C |
8.50 - 9.06 µin/in-°F @Temperature 68.0 - 212 °F |
|
| PEAK Werkstoff DISPAL S263 Aluminum Alloy, AlSi25Cu3Fe3Ni3MgCoTi, Condition T4 Excellent properties:abrasive stabilityhigh stiffness (E-modulus)resistance even at high temperaturesgood grindabilityPEAK DISPAL materials allow the manufacturing of pistons for highest operational.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 0.000 - 600 °C |
8.50 µin/in-°F @Temperature 32.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 0.000 - 600 °C |
8.50 µin/in-°F @Temperature 32.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 0.000 - 600 °C |
8.50 µin/in-°F @Temperature 32.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 0.000 - 600 °C |
8.50 µin/in-°F @Temperature 32.0 - 1110 °F |
|
| Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 21.0 - 871 °C |
8.50 µin/in-°F @Temperature 69.8 - 1600 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 21.0 - 871 °C |
8.50 µin/in-°F @Temperature 69.8 - 1600 °F |
|
| Haynes Hastelloy® N, weld metal as welded Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the man.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 625/ Alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Hastelloy® W alloy, gas metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Hastelloy® W alloy, shielded metal arc welds, aged 1000 hours at 650°C (1200°F) Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Hastelloy® W alloy, shielded metal arc welds, as-welded Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 25.0 - 300 °C |
8.50 µin/in-°F @Temperature 77.0 - 572 °F |
|
| Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts .. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 23.0 - 300 °C |
8.50 µin/in-°F @Temperature 73.4 - 572 °F |
|
| Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 23.0 - 300 °C |
8.50 µin/in-°F @Temperature 73.4 - 572 °F |
|
| Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 23.0 - 300 °C |
8.50 µin/in-°F @Temperature 73.4 - 572 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 23.0 - 300 °C |
8.50 µin/in-°F @Temperature 73.4 - 572 °F |
|
| Haynes Multimet® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 23.0 - 300 °C |
8.50 µin/in-°F @Temperature 73.4 - 572 °F |
|
| Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Hastelloy® alloy 188 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
|
| Haynes Hastelloy® alloy 718 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 24.0 - 760 °C |
8.50 µin/in-°F @Temperature 75.2 - 1400 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 24.0 - 760 °C |
8.50 µin/in-°F @Temperature 75.2 - 1400 °F |
|
| Haynes Hastelloy® C-22® alloy, SMAW weld, C-22 base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 24.0 - 760 °C |
8.50 µin/in-°F @Temperature 75.2 - 1400 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 20.0 - 100 °C |
8.50 µin/in-°F @Temperature 68.0 - 212 °F |
|
| ATI Allegheny Ludlum Stainless Steel AL-6XN® Alloy (UNS N08367), 40% Cold Work The AL-6XN® alloy is a superaustenitic stainless steel which was developed by Allegheny Ludlum Corporation. It exhibits far greater resistance to chloride pitting, crevice corrosion and stress-co.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 24.0 - 760 °C |
8.50 µin/in-°F @Temperature 75.2 - 1400 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 24.0 - 760 °C |
8.50 µin/in-°F @Temperature 75.2 - 1400 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GTAW spray weldment, 12.7 mm (1/2 in.) thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 21.0 - 871 °C |
8.50 µin/in-°F @Temperature 69.8 - 1600 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 593°C (1100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 23.0 - 300 °C |
8.50 µin/in-°F @Temperature 73.4 - 572 °F |
|
| Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
| CTE, linear | 15.3 µm/m-°C @Temperature 21.0 - 871 °C |
8.50 µin/in-°F @Temperature 69.8 - 1600 °F |
|
| Haynes Hastelloy® N, 1.14 mm sheet, heat treated at 1149°C (2100°F) Applications include containers for molten fluoride salts. Good oxidation resistance to hot fluoride salts at 705-870°C (1300-1600°F), good oxidation resistance in air.Data provided by the manufac.. |
|||