Thermal Properties | Metric | English | Comments |
---|---|---|---|
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 1.32 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 1.6 mm thick sheet, 1177°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 12.7 mm (1/2 in.) thick plate, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 25.4-50.8 mm forged bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 15% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 30% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 40% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 5% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, GTAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, GTAW, 6.35 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, GTAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, investment-cast, as-cast Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, sand cast, 1171°C heat treatment for 2 hours Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, SMAW, 12.7 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 35% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, SMAW, 3.2 mm sheet Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, SMAW, 9.5 mm plate Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductilit.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
Hardened Condition |
Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 12.7-50.8 mm hot-rolled bar, 1185°C heat treatment, water quenched Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 533.4 by 82.55 mm forging, stress relieved at 649°C (1200°F), air cooled Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 10% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 20% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 300 °C |
110 BTU-in/hr-ft²-°F @Temperature 572 °F |
|
Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 25% cold reduction Recommended for use in applications involving high stress at temperatures up to 816°C (1500°F), and moderate stresses up to 1093°C (2000°F). Excellent oxidation resistance, good ductility, and i.. |
|||
Thermal Conductivity | 15.9 W/m-K @Temperature 20.0 °C |
110 BTU-in/hr-ft²-°F @Temperature 68.0 °F |
|
Schmolz + Bickenbach Cryodur® 2363 (A-2) Cold Work Die Steel Description: Cryodur® 2363 is a cold-work steel developed for an excellent combination of wear resistance and toughness and Supplied in the annealed conditionCharacteristics: Good wear resistance; .. |