Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

LG Chemical LUPOY SR3108FC PC, Halogen Free Flame Retardance

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer LG Chemical
Trade Name LUPOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY SR3108FC PC, Halogen Free Flame Retardance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC, Halogen Free Flame Retardance, Light Reflectance, White Color OnlyApplication: LCD Back Light Unit partsCAS: 103598-77-2, 9003-56-9 and 13463-67-1Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 18 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 18 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ASTM D785
Tensile Strength, Yield 55.9 MPa

@Thickness 3.20 mm
 8110 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 100 %

@Thickness 3.20 mm
 100 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 88.3 MPa

@Thickness 3.20 mm
 12800 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.35 GPa

@Thickness 3.20 mm
 341 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 5.88 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 11.0 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 126 °C

@Thickness 6.40 mm
 >= 259 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 80.0 °C

@Thickness >=0.850 mm
 176 °F

@Thickness >=0.0335 in
110 °C

@Thickness >=1.50 mm
 230 °F

@Thickness >=0.0591 in
110 °C

@Thickness >=3.00 mm
 230 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 80.0 °C

@Thickness >=0.850 mm
 176 °F

@Thickness >=0.0335 in
100 °C

@Thickness >=1.50 mm
 212 °F

@Thickness >=0.0591 in
100 °C

@Thickness >=3.00 mm
 212 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 80.0 °C

@Thickness >=0.850 mm
 176 °F

@Thickness >=0.0335 in
120 °C

@Thickness >=1.50 mm
 248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
Flammability, UL94 V-1

@Thickness >=0.850 mm
 V-1

@Thickness >=0.0335 in
V-0

@Thickness >=1.50 mm
 V-0

@Thickness >=0.0591 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=1.50 mm
 15 - 30 sec

@Thickness >=0.0591 in
30 - 60 sec

@Thickness >=3.00 mm
 30 - 60 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 280 °C
482 - 536 °F
Injection Molding
Middle Barrel Temperature 260 - 290 °C
500 - 554 °F
Injection Molding
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Injection Molding
Nozzle Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Melt Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved