- Polymer Property : Flexural Yield Strength = 12800 psi
Polymer Property : Flexural Yield Strength = 12800 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Cycoloy® C1200 PC+ABS PC+ABS, excellent impact/high heat resistance. Low temperature ductility. For automotive, appliance and electrical components. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® ADX1016R PC (Europe-Africa-Middle East) Lexan Copolymer resin with improved chemical resistance, available only in limited colors. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| SABIC Innovative Plastics Lexan® EXL1036 PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1036 polycarbonate (PC) siloxane copolymer resin is a UV stabilized high viscosity grade designed for (co-)extrusion. This resin offers extreme low temperature (-60 C) ductility and good h.. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® EXL1330 PC Copolymer (Asia Pacific) Lexan* EXL1330 polycarbonate (PC) siloxane copolymer resin is a UV stabilized opaque injection molding (IM) and sheet extrusion grade. This resin offers extreme low temperature (-60 C) ductility in .. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1434T PC Copolymer Lexan* EXL1434T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding grade. This resin offers extreme low temperature (-40 C) ductility in combination with me.. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1434T PC Copolymer (Asia Pacific) Lexan* EXL1434T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding grade. This resin offers extreme low temperature (-40 C) ductility in combination with me.. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer Lexan* EXL1464T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flo.. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Asia Pacific) Lexan* EXL1464T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flo.. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL9112 PC Copolymer (Asia Pacific) Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temp. ductility. Non-chlorinated, non-brominated flame retardant product. UL rated V-0/5VA. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® FXE1414T PC Copolymer Clear PC-siloxane copolymer with excellent processability, for Visual fX capability in ""Energy"" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color pac.. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® FXM1414T PC Copolymer PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Lexan® EXL9132 PC Copolymer (Asia Pacific) Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temperature ductility, UV stabilized. Non-chlorinated, non-brominated flame retardant product. UL rated V0/5VA. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Asahi Kasei Tenac®-C 4510 Acetal Copolymer, General Purpose
(discontinued **) General-purpose grade, characterized by balanced flowability and mechanical properties.Applications: Gears, cams, hose joints, clips, switches, mechanical parts of audio and video equipment.This pro.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| KEP Kepital® F10 Standard Grade/High Viscosity Acetal Homopolymer Extrusion: electrical parts, machine/mechanical parts, industrial parts, automotive parts, applications, electronic data processing parts, thick-walledKepital® is a registered trademark of Korea .. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| KEP Kepital® F40 Standard Grade/Low Viscosity Acetal Homopolymer injection molding: electrical parts, machine/mechanical parts, industrial parts, automotive applications, electronic data processing.Kepital® is a registered trademark of Korea Engineering Plasti.. |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY HI1002ML PC, High Impact Description: Injection Molding, PC, General Purpose, High Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 9046-16-6Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| LG Chemical Lupox® TE5000GH PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional StabilityApplication: Automotive (Door Garnish)CAS No. 24968-12-5 and 103598-77-2Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC LNP* Lubricomp* Lexan_WR2210 compound is an alternative polymeric wear additive technology. No silicones, superior processability/part appearance. Flow similar to LEXAN 121. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3020A Polycarbonate with Heat Stabilizer PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020A is a high flow grade with heat stabilizers.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3020IR Polycarbonate with Heat Stabilizer PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020IR is a high flow grade with added heat stabilizers, separating materials and stain.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3020PJ Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020PJ is a high flow grade.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3022PJ Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3022PJ is a general use grade.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3027IR Polycarbonate TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3027PJ Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3027PJ is an extrusion grade.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® D202 PBT, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOTUF MF0049I PP (Europe-Africa-Middle East) LNP* THERMOTUF* MF0049I is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features include; Flame Retardant, Chemically Coupled. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66 Noryl GTX* GTX942 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is designed to have high melt flow for large part/thinwall injection molding. The material is designed to h.. |
|||
| Flexural Yield Strength | 88.0 MPa | 12800 psi | 6.4 mm; ASTM D790 |
| SABIC Innovative Plastics NORYL PVX0800 PPE NORYL* PVX0800 resin is a high flow, V0 = 1.5 mm grade, suitable for a variety of electronics applications. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| PlastxWorld CEVIAN® SERG1 10% GF ABS Glass fiber reinforced and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Cheng Yu Plastic SW10 POM/PTFE |
|||