Polymer Property : Melt Flow = 18 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most.

Physical Properties	Metric	English	Comments
Melt Flow	18 g/10 min	18 g/10 min	ASTM D1238
Multibase Multi-Pro® 3018 TU Polypropylene Talc Filled, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingUses: Automotive Under the HoodInformation provided by Multibase
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 230 °C	18 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
RheTech Products F22-01 20% Glass Fiber/Mineral Co-Reinforced Polypropylene, Black Applications: Support ductsHousingsBattery traysInjection molding conditions reported in table.Information provided by RheTech Products.
Melt Flow	18 g/10 min @Load 5.00 kg, Temperature 260 °C	18 g/10 min @Load 11.0 lb, Temperature 500 °F	[cm^3/10 min] Melt Volume Rate; ISO 1133
SABIC Innovative Plastics Cycoloy® C2100HF PC+ABS (Europe-Africa-Middle East) CYCOLOY C2100HF is a flame retardant blend with improved flow, specially developed to meet the stringent requirements of mains current carrying applications.This data was supplied by SABIC-IP for th..
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 260 °C	18 g/10 min @Load 4.76 lb, Temperature 500 °F	ASTM D1238
SABIC Innovative Plastics Cycoloy® CY6120 PC+ABS (Asia Pacific) Non-chlorinated and non-brominated flame retardant PC/ABS featuring good flow and impact properties. UL-94 V0 listed at 1.2mm intended for various thin wall applications.
Melt Flow	18 g/10 min @Load 1.20 kg, Temperature 300 °C	18 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Ravago Manufacturing Americas Hylex® P1018FRVNHE Polycarbonate Polycarbonate, 18 Melt Flow, Flame Retardant, Non HalogenatedInformation provided by Ravago.
Melt Flow	18 g/10 min @Load 1.20 kg, Temperature 300 °C	18 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
PTS Tristar® PC-10R-(18) 18 MFI Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS).
Melt Flow	18 g/10 min @Load 1.20 kg, Temperature 300 °C	18 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer (Asia Pacific) 18 MFR LEXAN High Flow Ductile Copolymer UV-stabilized, available in transparent colors only
Melt Flow	18 g/10 min @Load 5.00 kg, Temperature 200 °C	18 g/10 min @Load 11.0 lb, Temperature 392 °F	Procedure A Condition G; ASTM D1238
Network Polymers NPS 80-1800 Crystal Polystyrene Description: Injection Molding Grade, High Melt FlowInformation provided by Network Polymers Inc.
Melt Flow	18 - 30 g/10 min @Load 1.20 kg, Temperature 300 °C	18 - 30 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Polymer Resources PC-UV4-[color]-1 Polycarbonate, UV-stabilized, Easy Flow with Mold Release Polycarbonate, UV-stabilized, Easy Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informa..
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 343 °C	18 g/10 min @Load 4.76 lb, Temperature 649 °F	ASTM D1238
Solvay Specialty Polymers Udel® P-3700 HC Polysulfone (PSU)  (Unverified Data**) Udel P-3700 HC is a high-clarity grade of polysulfone (PSU) that is nearly water-white in color. This grade was designed to eliminate the yellow cast and provide design flexibility and improved aest..
Melt Flow	18 g/10 min @Load 1.20 kg, Temperature 300 Â°C	18 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238
LG Chemical Lupoy 1201-18 Polycarbonate Resin Description: LUPOY PC 1201-18 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength...
Melt Flow	18 - 22 g/10 min @Load 2.16 kg, Temperature 235 Â°C	18 - 22 g/10 min @Load 4.76 lb, Temperature 455 Â°F	ASTM D1238
Gromax PBT 1100-211M Product Description: PBT unreinforced middle viscosity injection molding grade. Characteristics:Excellent electrical property Excellent temperature resistance, high heat distortion temperature. Exce..
Melt Flow	18 g/10 min @Load 3.80 kg, Temperature 260 Â°C	18 g/10 min @Load 8.38 lb, Temperature 500 Â°F	ASTM D1238
LTL Color Compounds ColorFastÂ® PCT1000 PC/PET Alloy PC/PET alloy with outstanding chemical resistance and impact strengthAll information provided by LTL Color Compounders, Inc.
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 230 Â°C	18 g/10 min @Load 4.76 lb, Temperature 446 Â°F	Condition L; ASTM D1238
LyondellBasell Hifaxâ„¢ CB272 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CB272 high melt flow, 900 MPa flexural modulus, low CLTE, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of rigidity and dime..
Melt Flow	18 g/10 min @Load 1.20 kg, Temperature 300 Â°C	18 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238
SABIC Innovative Plastics PC1803R PC (Asia Pacific) PC1803R resin is a medium-high flow (MFR = 18 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 230 Â°C	18 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133
SABIC Innovative Plastics SABIC PPCOMPOUND 19T1020 PP SABICÂ® PPcompound 19T1020 is a general purpose, talc filled, heat stabilized homopolymer polypropylene compound. This compound exhibits high flow and is suitable for injection molding application..
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 265 Â°C	18 g/10 min @Load 4.76 lb, Temperature 509 Â°F	ASTM D1238
SABIC Innovative Plastics ValoxÂ® 830F PBT+PET (Europe-Africa-Middle East) PBT+PET, 30% Glass, Mold Release, Heat Stabilized, For food contact applications
Melt Flow	18 g/10 min @Load 10.0 kg, Temperature 220 Â°C	18 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ISO 1133
Styrolution NovodurÂ® M201AS ABS Novodur M201AS is a medium impact, high gloss injection molding grade with improved chemical resistanceInformation provided by Styrolution
Melt Flow	18 g/10 min	18 g/10 min	ASTM D1238
Styron PULSEâ„¢ 2000 EZ PC/ABS Engineering Resin Overview: PULSE 2000 Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can wi..
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 230 °C	18 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3476 is a homopolymer polypropylene for use in the process of multi-filaments, high tenacity continuous filament yarn and fine denier staple fibers. Information provided ..
Melt Flow	18 g/10 min	18 g/10 min	ASTM D1238
A. Schulman POLYFORT™ PP 3719 Impact Copolymer Polypropylene DescriptionPolyfort® PP 3719 is a UV stabilized impact copolymer polypropylene compound. Information provided by A. Schulman.
Melt Flow	18 g/10 min	18 g/10 min	Condition G; ASTM D1238
American Polymers API 395 Polystyrene API 395 is one of the highest flowing crystal polystyrenes commercially available. It is produced in pellet form for injection molding and compounding. This material is designed for hard to fill ..
Melt Flow	18 g/10 min	18 g/10 min	ISO 1133
Tisan TISOPLEN® 20% Calcite Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois..
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 330 °C	18 g/10 min @Load 4.76 lb, Temperature 626 °F	ISO 1133
Covestro Apec® 1897 Polycarbonate Easy flowingeasy to demoldUV-stabilizedsoftening temperature (VST/B 120)=182 °CPreprocessingMax. Water content
Melt Flow	18 g/10 min @Load 5.00 kg, Temperature 260 °C	18 g/10 min @Load 11.0 lb, Temperature 500 °F	ISO 1133
Covestro Makroblend® DP UT6003 Polycarbonate + PBT, Impact Grade Developmental product(PC+PBT)-blendimpact modifiedUV-stabilizedinjection molding grade Makroblend DP UT6003* offers an exceptional low-temperature impact strength, good flowability and excellent c..
Melt Flow	18 g/10 min @Load 2.16 kg, Temperature 230 °C	18 g/10 min @Load 4.76 lb, Temperature 446 °F
ExxonMobil Mytex™ AS23K(W)-01 Talc filled compounded polypropylene produced for automotive interior applicationsInformation provided by ExxonMobil Chemical
Melt Flow	18 g/10 min	18 g/10 min	ISO 1133
Addiplast Addilene J 520 M20 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast.
Melt Flow	18 g/10 min @Load 5.00 kg, Temperature 300 °C	18 g/10 min @Load 11.0 lb, Temperature 572 °F	ASTM D1238
BLUESTAR LXS 314 G20 PPE-HIPS, 20% Glass Filled Typical Applications: Water industrial partsInformation provided by Polymer Technology and Services, LLC (PTS).