- Polymer Property : Flexural Yield Strength = 88.3 MPa
Polymer Property : Flexural Yield Strength = 88.3 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Kolon Kocetal® DP301 Modified Grade Acetal Copolymer
(discontinued **) Thermal properties: Kocetal has excellent heat stability; heat degradation is little under long term and high temperature application, compared to other POM. Maximum applicable temperature of produ.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Plenco Valite 1246-18X Novolac Phenolic, Granular, Injection Molded
(discontinued **) This Valite product has been replaced by Plenco 4246. Data provided by Plenco.VALITE 1246-18X is a black two-stage, medium heat resistant phenolic molding compound. It has excellent electrical, mol.. |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
1mm/min; ASTM D790 |
| LG Chemical LUCON PN9009 PPS+MF Injection Molding Grade, PPS+MF, High Thermal Conductivity, Chemical Resistance, High Heat ResistanceApplication: Electrical or Electronic Parts (Heat sink, LED etc.) Motor HousingCAS No. 25212-74-2.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | DIN 53455; ASTM D790 |
| Kolon KOPA® KN173HI2 High Impact Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| LG Chemical LUMIPLAS LD590 Light diffusion ABS Description: Injection Molding, Light diffusion, Medium ImpactApplication: (LED) Lamp Cover, Signboard Lighting Decoration of Electronic DeviceCAS No. 9010-94-0Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| KEP Kepital® F10 Standard Grade/High Viscosity Acetal Homopolymer Extrusion: electrical parts, machine/mechanical parts, industrial parts, automotive parts, applications, electronic data processing parts, thick-walledKepital® is a registered trademark of Korea .. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| KEP Kepital® F40 Standard Grade/Low Viscosity Acetal Homopolymer injection molding: electrical parts, machine/mechanical parts, industrial parts, automotive applications, electronic data processing.Kepital® is a registered trademark of Korea Engineering Plasti.. |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical Lupox® SG3250A PBT+PET+MF25% Description: Injection Molding, PBT+PET+MF25%, Good SurfaceApplication: Automotive (Head Lamp Bezel)CAS No. 24968-12-5, 25038-59-9 and 14807-96-6Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| LG Chemical Lupox® TE5000G PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional Stability, Good WeatherabilityApplication: Automotive (Door Garnish, Door Handle)CAS No. 24968-12-5 and 103598-77-2Information provid.. |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| LG Chemical Lupox® TE5000SZ PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional StabilityApplication: Automotive ItemCAS No. 137050-02-03, 26062-94-2 and 103598-77-2Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| LG Chemical Lupox® TE5006F PET+PC Description: Injection Molding, PET+PC, Flame Retardant, GWIT, CTIApplication: IT/OA, E&E (Connector)CAS No. 68928-70-1, 103598-77-2, 25038-59-9 and 1309-64-4Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY HI1002ML PC, High Impact Description: Injection Molding, PC, General Purpose, High Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 9046-16-6Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY SC3154 PC+GF15% Description: Injection Molding, PC+GF15%, General Purpose, Good Toughness, Dimensional Stability, Good Surface, Chemical ResistanceApplication: Mobile Phone Housing and ComponentsInformation provide.. |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
5mm/min; ASTM D790 |
| LG Chemical Lupox® TE5000GH PBT+PC Description: Injection Molding, PBT+PC, High Impact, Dimensional StabilityApplication: Automotive (Door Garnish)CAS No. 24968-12-5 and 103598-77-2Information provided by LG Chemical |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 3.20 mm |
12800 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| LG Chemical LUPOY GN5001RF PC/ABS, Halogen Free Flame Retardant Description: Injection Molding, PC/ABS, Halogen Free Flame Retardant, Good FlowApplication: E&E (TV, Navigation Housing)CAS: 103598-77-2, 9003-56-9 and 181028-79-5Information provided by LG Chemical.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3020A Polycarbonate with Heat Stabilizer PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020A is a high flow grade with heat stabilizers.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3020IR Polycarbonate with Heat Stabilizer PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020IR is a high flow grade with added heat stabilizers, separating materials and stain.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3020U UV Stable Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3020U is a high flow, UV Stable grade.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3022PJ Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3022PJ is a general use grade.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3027PJ Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3027PJ is an extrusion grade.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3027PU(X) Polycarbonate PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3027PU(X) is an extrusion grade.Information provided by Samyang. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3030U Polycarbonate, UV Stabilized TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Shinkong Synthetic Fibers Shinite® D202 PBT, Fire Retardant Information from Shinkong Synthetic Fibers Corp. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Samyang Trirex® 3017IR Polycarbonate with Heat Stabilizer PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3017IR is a super high flow grade with added heat stabilizers, separating materials and.. |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Cheng Yu Plastic PP236G1 Polypropylene, 10% Glass Fiber |
|||
| Flexural Yield Strength | 88.3 MPa | 12800 psi | ASTM D790 |
| Cheng Yu Plastic SW10 POM/PTFE |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
ASTM D790 |
| Bhansali Engineering Abstron IMC-45V ABS-PC Alloy ABS-polycarbonate alloys for High service temperature applications.Information provided by Bhansali |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
ASTM D790 |
| Bhansali Engineering Abstron IMC-45V ABS-PC Alloy ABS-polycarbonate alloys for High service temperature applications.Information provided by Bhansali |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IMG1120 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
| Flexural Yield Strength | 88.3 MPa @Thickness 6.40 mm |
12800 psi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IMG1120 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||