SABIC Innovative Plastics Cycolac® MG34LGHF ABS

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® MG34LGHF ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Low gloss, high flow ABS for unpainted interior applications.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D 792
Density 1.03 g/cc
0.0372 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 1.0 %

@Temperature 23.0 °C
1.0 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 12 g/10 min

@Load 3.80 kg,
Temperature 230 °C
12 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D 1238
40 g/10 min

@Load 10.0 kg,
Temperature 220 °C
40 g/10 min

@Load 22.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.0 MPa
4500 psi
5 mm/min; ISO 527
32.0 MPa
4640 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 38.0 MPa
5510 psi
5 mm/min; ISO 527
39.0 MPa
5660 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 25 %
25 %
Type I, 5 mm/min; ASTM D 638
25 %
25 %
5 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D 638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 2.13 GPa
309 ksi
5 mm/min; ASTM D 638
2.26 GPa
328 ksi
1 mm/min; ISO 527
Flexural Yield Strength 61.0 MPa
8850 psi
2 mm/min; ISO 178
62.0 MPa
8990 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.13 GPa
309 ksi
1.3 mm/min, 50 mm span; ASTM D 790
2.14 GPa
310 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.370 J/cm

@Temperature -30.0 °C
0.693 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
2.13 J/cm

@Temperature 23.0 °C
3.99 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
16.0 kJ/m²

@Temperature 23.0 °C
7.61 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.60 J/cm²

@Temperature 23.0 °C
7.61 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 25.0 J

@Temperature 23.0 °C
18.4 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
82.0 °C

@Thickness 3.20 mm
180 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 97.0 °C
207 °F
Rate B/50; ISO 306
98.0 °C
208 °F
Rate B/50; ASTM D 1525
101 °C
214 °F
Rate B/120; ISO 306