Polymer Property : Flexural Yield Strength = 8990 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	62.0 MPa	8990 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® MG34LG ABS Automotive: Low gloss ABS for unpainted interior applications.
Flexural Yield Strength	62.0 MPa	8990 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics Cycolac® MG34LGHF ABS Low gloss, high flow ABS for unpainted interior applications.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	62.0 MPa	8990 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® S702 ABS (Europe-Africa-Middle East) CYCOLAC S702 is a high impact ABS combined with a good flow. This material is developed for enclosures and housings found in appliances and automotive industries.This data was supplied by SABIC-IP f..
Flexural Yield Strength	62.0 MPa	8990 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® S702S ABS (Europe-Africa-Middle East) CYCOLAC S702S is a high impact ABS combined with a good flow. This material is developed for enclosures and housings found in appliances and automotive industries. Cycolac S702S is anti-dust equiped..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Ineos Nova 2580 General Purpose Crystal Polystyrene (discontinued **) High speed molding, Improved crack resistanceApplications: Cutlery, Consumer electronicsExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the physical and optic..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Ineos Nova 2504 General Purpose Crystal Polystyrene (discontinued **) Good blending resin, Good balance of flow, strength and heat resistance, USP Class VI Applications: Consumer electronics, HousewaresExposure to gamma radiation in the 2.02-6.06 megarad range has no ..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Ineos Nova 2510 General Purpose Crystal Polystyrene (discontinued **) High speed molding, Improved crack resistance, USP Class VIApplications: Cutlery, Light louvers, RazorsExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the phy..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Ineos Nova 2511 General Purpose Crystal Polystyrene (discontinued **) High speed molding, Improved crack resistance, USP Class VIApplications: Cutlery, Light louvers, RazorsExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the phy..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Kleerdex Kydex® 130 Acrylic/PVC Thermoplastic Sheet (discontinued **) Decorative thermoplastic sheetApplications: Appliances, laminations, electronics, in-store displays, medical devices, equipment housings, dental equipmentFeatures: For deep to hard to form parts or ..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Kleerdex Kydex® P26 Acrylic/PVC Extrusion Compound (discontinued **) High impact profile extrusion compoundApplications: Extruded profiles for recreational equipment, medical equipment, business equipment, profiles for use in the interior of commercial aircraft.Featu..
Flexural Yield Strength	62.0 - 94.0 MPa	8990 - 13600 psi	Average value: 75.7 MPa Grade Count:21
Overview of materials for Phenolic, Novolac, Impact Grade, Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Impact Grade, Filled". Each property range of values reported is minimum and maximum ..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Plenco 5314 Black (COM) Impact Grade Phenolic Molding Compound (discontinued **) Plaslok 5314 is the replacement material for the former Union Carbide BMMA-5314. It is a two-stage, impact grade phenolic molding compound suitable for compression, transfer or injection molding of..
Flexural Yield Strength	62.0 MPa	8990 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics PREVEX W20 PPE+PS (Asia Pacific) Automotive. PPE alloy. High flow/impact. Instrument panels and interior trim components. HDT 210F.
Flexural Yield Strength	62.0 MPa	8990 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® V2105U PBT Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Flexural Yield Strength	62.0 MPa	8990 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp PH0700B PA 6 LNP* Thermocomp* PH0700B is a Nylon 6 base resin containing Tungsten. Characteristics are High Specific Gravity.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	62.0 MPa	8990 psi	2 mm/min; ISO 178
SABIC Innovative Plastics ValoxÂ® V2105U PBT (Europe-Africa-Middle East) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Flexural Yield Strength	62.0 MPa	8990 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics NORYL EM7100 PPE+PS Automotive interiors. 200F DTUL. Excellent processability/economy. Good impact/mechanicals vs styrenics. Trim/instrument panel components.
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Tipco Tipcolite® TG 617 Phenolic Compound, Mineral & Wood Flour, Medium Flow & High Electrical Properties Medium Flow Phenolic Compound, Reinforced with Mineral & Wood FlourApplications: Electrical & ElectronicsProcessing: Compression & TransferInformation provided by the Manufacturer, Tipco Industrie..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Eastman Tritan MX710 Copolyester Eastman Tritan Copolyester MX710 is an amorphous product with excellent appearance and clarity. Eastman Tritan Copolyester MX710 has many outstanding features that include excellent toughness, hydr..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Eastman Tritan TX1000 Copolyester Eastman Tritan TX1000 is an amorphous copolyester with excellent appearance and clarity. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistanc..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Eastman Tritan TX1001 Copolyester Eastman Tritan TX1001 is an amorphous copolyester with excellent appearance and clarity. Eastman Tritan TX1001 contains a mold release derived from vegetable based sources. Its most outstanding fe..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Covestro Baydur® 726 IBS Polyurethane Structural Foam RIM, Density 55 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. IBS = Interactive Blowing System RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience ..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Ineos Nova 5100 High Impact Polystyrene (discontinued **) Good balance of toughness and rigidity, USP Class VIApplications: Spools and reels, Thermoformed and molded packaging, Photographic cartridges, AppliancesProperties were determined on injection mold..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Ineos Nova 5104 High Impact Polystyrene (discontinued **) Good balance of toughness and rigidity, USP Class VIApplications: Spools and reels, Thermoformed and molded packaging, Photographic cartridges, AppliancesProperties were determined on injection mold..
Flexural Yield Strength	62.0 MPa	8990 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Valox® V2105U PBT (Asia Pacific) Unreinforced, Wear resistant, UV Stabilized PBT designed for outdoor, agricultural, industrial and automotive applications. This grade has very high impact strength to stiffness ratio.
Flexural Yield Strength	62.0 - 69.0 MPa	8990 - 10000 psi	ASTM D790
Kleerdex Kydex® 100 AS Acrylic/PVC Thermoplastic Sheet (discontinued **) Anti-static sheetApplications: Housings for equipment such as photocopy machines, instrument panels, computers, keyboards, telephones, internal parts for electrical and electronic equipment, medical..
Flexural Yield Strength	62.0 MPa	8990 psi	ASTM D790
Plaslok 5314 Black (COM) Impact Grade Phenolic Molding Compound (discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 5314 is the replacement material for ..
Flexural Yield Strength	62.0 MPa	8990 psi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp FF006 PE LNP Thermocomp FF-1006 is a glass filled Polyethylene.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	62.0 MPa	8990 psi	2.6 mm/min, 100 mm span; ASTM D790
SABIC Innovative Plastics PREVEX W20 PPE+PS Automotive. PPE alloy. High flow/impact. Instrument panels and interior trim components. HDT 210F.