Eastman Tenite 383A-08 Cellulose Acetate Propionate  (discontinued **)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 383A-08 Cellulose Acetate Propionate  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
8% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0020 - 0.0060 in/in

@Thickness 0.126 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 37.0 MPa
5370 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 1.74 GPa
252 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Charpy Impact, Notched 1.42 J/cm²
6.76 ft-lb/in²
0.440 J/cm²

@Temperature -30.0 °C
2.09 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 99.0 µm/m-°C

@Temperature 20.0 °C
55.0 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 134 µm/m-°C

@Temperature 20.0 °C
74.4 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Vicat Softening Point 95.0 °C
203 °F
Glass Transition Temp, Tg 110 °C
230 °F
Processing Properties Metric English Comments
Melt Temperature 240 - 250 °C
464 - 482 °F