Polymer Property : Flexural Yield Strength = 8850 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	61.0 MPa	8850 psi	ASTM D790
Nylene® 603 Nylon 6, Extrusion Grade Dry as molded. Extrusion grade. Nylene 603 is a plasticized, high residual monomer resin designed for extrusion applications requiring excellent flexibility, high strength and good abrasion resist..
Flexural Yield Strength	61.0 MPa	8850 psi	2 mm/min; ISO 178
SABIC Innovative Plastics Cycolac® MG34LGHF ABS Low gloss, high flow ABS for unpainted interior applications.This data was supplied by SABIC-IP for the Americas region.
Flexural Yield Strength	61.0 MPa	8850 psi	ASTM D790
Ineos Nova 2100 General Purpose Crystal Polystyrene (discontinued **) Relative high heat resistance, Improved crack resistance, Good strengthApplications: Foam extrusion, Biaxially oriented sheet, Thermoforming applications, Molded packagingExposure to gamma radiation..
Flexural Yield Strength	61.0 - 83.2 MPa	8850 - 12100 psi	Average value: 74.2 MPa Grade Count:7
Overview of materials for Phenolic, Novolac, Flock Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Flock Filled". Each property range of values reported is minimum and maximum values o..
Flexural Yield Strength	61.0 MPa	8850 psi	ASTM-D790
Ineos ABS LustranÂ® 256/LustranÂ® 752 Blended ABS Resin 50/50 pellet blend of LustranÂ® 256 ABS and high-impact LustranÂ® 752 ABS
Flexural Yield Strength	61.0 MPa @Strain 3.50 %	8850 psi @Strain 3.50 %	d.a.m., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® DP 2325 H3.0 DUS031 000000 Nylon 66 PA 66, non-reinforced, injection molding, improved flowability, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Yield Strength	61.0 MPa	8850 psi	at 5% strain; ASTM D790
Ineos ABS TriaxÂ® 1220 S ABS + Polyamide Blend, Extrusion, Conditioned Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
Flexural Yield Strength	61.0 MPa	8850 psi	at 5% strain; ASTM D790
Ineos ABS TRIAXÂ® 1220 S ABS/Nylon Blend, As Conditioned Extrusion and injection molding grade with good stress corrosion cracking resistance, good chemical resistance (fuel, cleaning agents), high impact and notched impact strength, good acoustical dampi..
Flexural Yield Strength	61.0 MPa	8850 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP HH0420A PA11 LNP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity.
Flexural Yield Strength	61.0 MPa	8850 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer containing PTFE / Silicone. Added features include: Inernally Lubricated
Flexural Yield Strength	61.0 MPa	8850 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP004AXP POM (Europe-Africa-Middle East) LNP* LUBRICOMP* KP004AXP is a compound based on Acetal Homopolymer containing PTFE, Silicone. Added features include Internally Lubricated.
Flexural Yield Strength	61.0 MPa	8850 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP MX06404 PP LNP LUBRICOMP* MX06404 is a compound based on Polypropylene resin containing 20% Glass Fiber and 15% PTFE. Added features of this material include: Heat Stabilized, Low Extractable, Wear Resistant...
Flexural Yield Strength	61.0 MPa	8850 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NWR5810 PPE+HIPS (Europe-Africa-Middle East) LNP* Lubricomp* Noryl_NWR5810 compound is a 10% PTFE filled PPE+PS. High flow and good impact. Applications requiring wear resistance/lubricity. Electronics.
Flexural Yield Strength	61.0 MPa	8850 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NWR5810 PPE+PS LNP* Lubricomp* Noryl_NWR5810 compound is a 10% PTFE filled PPE+PS. High flow and good impact. Applications requiring wear resistance/lubricity. Electronics.
Flexural Yield Strength	61.0 MPa	8850 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP WP004 PBT (Europe-Africa-Middle East) LNP* Lubricomp* WP004 is a compound based on Polybutylene Terephalate resin containing PTFE, Silicone. Added features include ; Internally Lubricated.
Flexural Yield Strength	61.0 MPa	8850 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS (Asia Pacific) LNP* Stat-loy* AF3009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Antistat, Flame Retardant.
Flexural Yield Strength	61.0 MPa	8850 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP HH0420A PA11 LNP* THERMOCOMP* HH0420A is a compound based on Nylon 11 containing proprietary fillers. Added features of this material are High Specific Gravity.
Flexural Yield Strength	61.0 MPa	8850 psi	ASTM D790
Tipco Tipcolite® THD 411 Phenolic Compound, Mica, Asbestos & Cellulose, Medium Flow & High Electrical Properties Medium Flow Phenolic Compound, Reinforced with Mica, Asbestos & CelluloseApplications: Electrical & ElectronicsProcessing: Compression MoldingInformation provided by the Manufacturer, Tipco Industr..
Flexural Yield Strength	61.0 MPa	8850 psi	2 mm/min; ISO 178
Eurostar Staramide P1000IX3 PA6, Impact Modified, Injection Molded Staramide P1000IX3 is an Impact Modified, Polyamide 6 Injection Molding Resin (also known as P1000HI020 or Star X 2020)Information provided by Eurostar.
Flexural Yield Strength	61.0 MPa	8850 psi	2 mm/min; ISO 178
SABIC Innovative Plastics LNP Thermotuf P1000IX3 PA 6 (Europe-Africa-Middle East) LNP* THERMOTUF* P1000IX3 is a compound based on PA6 resin containing Impact Modifier. Added features include : High Impact.This data was supplied by SABIC-IP for the Europe-Africa-Middle East regio..
Flexural Yield Strength	61.0 MPa	8850 psi	6.4 mm; ASTM D790
SABIC Innovative Plastics NORYL FN215X PPE+PS Structural foam resin. 170F (77C) HDT. Improved reliability and productivity. All values at 20% weight reduction.