Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Molded/Extruded

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate; Molded/Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Molded/Extruded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate; Molded/Extruded". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 0.923 - 1.21 g/cc
0.0333 - 0.0437 lb/in³
Average value: 0.944 g/cc Grade Count:94
Apparent Bulk Density 0.545 - 0.577 g/cc
0.0197 - 0.0208 lb/in³
Average value: 0.569 g/cc Grade Count:4
Particle Size 5.00 - 1000 µm
5.00 - 1000 µm
Average value: 494 µm Grade Count:7
Viscosity 9300 - 9300 cP

@Temperature 190 - 190 °C
9300 - 9300 cP

@Temperature 374 - 374 °F
Average value: 9300 cP Grade Count:1
Environmental Stress Crack Resistance 500 - 1000 hour
500 - 1000 hour
Average value: 667 hour Grade Count:6
Vinyl Acetate Content 2.00 - 40.0 %
2.00 - 40.0 %
Average value: 19.4 % Grade Count:79
Melt Flow 0.150 - 850 g/10 min
0.150 - 850 g/10 min
Average value: 62.6 g/10 min Grade Count:103
Mechanical Properties Metric English Comments
Hardness, Shore A 53.0 - 98.0
53.0 - 98.0
Average value: 85.8 Grade Count:62
Hardness, Shore D 15.0 - 67.0
15.0 - 67.0
Average value: 36.7 Grade Count:56
Tensile Strength, Ultimate 1.90 - 26.8 MPa
276 - 3890 psi
Average value: 12.7 MPa Grade Count:70
1.40 - 51.0 MPa

@Temperature -20.0 - 49.0 °C
203 - 7400 psi

@Temperature -4.00 - 120 °F
Average value: 19.8 MPa Grade Count:11
Tensile Strength, Yield 2.50 - 28.3 MPa
363 - 4110 psi
Average value: 7.13 MPa Grade Count:24
Elongation at Break 50.0 - 1300 %
50.0 - 1300 %
Average value: 653 % Grade Count:81
400 - 900 %

@Temperature -20.0 - 49.0 °C
400 - 900 %

@Temperature -4.00 - 120 °F
Average value: 607 % Grade Count:11
Modulus of Elasticity 0.0110 - 0.700 GPa
1.60 - 102 ksi
Average value: 0.0939 GPa Grade Count:21
0.0460 - 0.345 GPa

@Temperature -20.0 - -20.0 °C
6.67 - 50.0 ksi

@Temperature -4.00 - -4.00 °F
Average value: 0.157 GPa Grade Count:11
Flexural Modulus 0.00190 - 0.345 GPa
0.276 - 50.0 ksi
Average value: 0.0630 GPa Grade Count:62
0.00620 - 0.503 GPa

@Temperature -20.0 - 49.0 °C
0.899 - 73.0 ksi

@Temperature -4.00 - 120 °F
Average value: 0.128 GPa Grade Count:11
Secant Modulus 0.0210 - 1.25 GPa
3.05 - 181 ksi
Average value: 0.496 GPa Grade Count:4
Tensile Impact Strength 2.50 - 945 kJ/m²
1.19 - 450 ft-lb/in²
Average value: 536 kJ/m² Grade Count:17
Compression Set 39.0 - 60.0 %
39.0 - 60.0 %
Average value: 50.1 % Grade Count:11
70.0 - 100 %

@Temperature 70.0 - 70.0 °C
70.0 - 100 %

@Temperature 158 - 158 °F
Average value: 89.9 % Grade Count:11
Thermal Properties Metric English Comments
Melting Point 52.0 - 104 °C
126 - 219 °F
Average value: 85.8 °C Grade Count:67
Vicat Softening Point 23.0 - 127 °C
73.4 - 261 °F
Average value: 64.9 °C Grade Count:66
Brittleness Temperature -100 - -40.0 °C
-148 - -40.0 °F
Average value: -84.7 °C Grade Count:42
Flammability, UL94 HB
HB
Grade Count:3
Ring & Ball Softening Point 76.0 - 220 °C
169 - 428 °F
Average value: 113 °C Grade Count:15
Optical Properties Metric English Comments
Transmission, Visible 80.0 %
80.0 %
Average value: 80.0 % Grade Count:6
Electrical Properties Metric English Comments
Electrical Resistivity 400 - 1.00e+15 ohm-cm
400 - 1.00e+15 ohm-cm
Average value: 7.50e+14 ohm-cm Grade Count:4
Comparative Tracking Index 600 V
600 V
Average value: 600 V Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 121 - 204 °C
250 - 399 °F
Average value: 163 °C Grade Count:12