Polymer Property : Tensile Strength, Yield = 2.50 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	2.50 MPa	362 psi	at 200%, post cured- 2 hours at 177°C
Multibase SILASTIC® C7-4550 CADOX TS-50S Dow-Corning Biomedical Grade ETR Elastomer Information provided by Multibase
Tensile Strength, Yield	2.50 - 28.3 MPa	363 - 4110 psi	Average value: 7.13 MPa Grade Count:24
Overview of materials for Ethylene Vinyl Acetate Copolymer (EVA), Molded/Extruded This property data is a summary of similar materials in the MatWeb database for the category "Ethylene Vinyl Acetate; Molded/Extruded". Each property range of values reported is minimum and maximum ..
Tensile Strength, Yield	>= 2.50 MPa	>= 363 psi
Trelleborg Offshore Vikotherm™ 73961 Insulative Elastomer Vikotherm™ is a rubber elastomer chemically modified to provide very high insulating characteristics while maintaining its inherent rubber properties in respect of seawater resistance, pressure res..
Tensile Strength, Yield	>= 2.50 MPa	>= 363 psi
Trelleborg Offshore Vikotherm™ 73982 Insulative Elastomer Vikotherm™ is a rubber elastomer chemically modified to provide very high insulating characteristics while maintaining its inherent rubber properties in respect of seawater resistance, pressure res..
Tensile Strength, Yield	2.50 MPa	362 psi	at 150% Elongation, maximum
Dow Corning SILASTIC® LS 4-9062 FLUOROSILICONE RUBBER 65 durometer, off-white, uncatalysed, fluorosilicone base.Information provided by Dow Corning
Tensile Strength, Yield	2.50 MPa @Strain 100 %	363 psi @Strain 100 %	ISO 527-1/-2
Covestro Desmopan® DP 1960AW Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Tensile Strength, Yield	2.50 MPa @Strain 100 %	363 psi @Strain 100 %	ISO 527-1/-2
Covestro Desmopan® DP 1966AW Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro.
Tensile Strength, Yield	2.50 MPa @Strain 100 %	363 psi @Strain 100 %	ISO 527-1/-2
Covestro Desmopan® DP 3070AU Polyurethane injection molding gradefree from plasticizersApplicationInjection molded engineering partshard - soft systemsAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially ..
Tensile Strength, Yield	2.50 MPa	363 psi
Dow AFFINITY™ SM 8250 Polyolefin Plastomer AFFINITY® SM 8250 polyolefin plastomer is an alpha-olefin resin that offers excellent performance in injection molded clear or colored flexible durable parts. It exhibits excellent clarity and flex..
Tensile Strength, Yield	2.50 MPa	363 psi	508 mm/min; ASTM D638
Dow Engage® 8452 Polyolefin Elastomer Description: Engage® 8452 polyolefin elastomer is an ethyleneoctene copolymer that offers excellent toughness, softness, and optical properties. It has excellent compatibility with other polyolefin..
Tensile Strength, Yield	2.50 MPa	363 psi
ACC MM282 Specialist Molding 2-Part Condensation Cure Part of the Amber Chemical Group. Data provided by manufacturer.
Tensile Strength, Yield	2.50 MPa	363 psi
ACC MM911 Condensation Cure 2-Part Molding Rubber Part of the Amber Chemical Group. Data provided by manufacturer.Characteristics: high tear strength, picks up extremely fine details, low viscosity, good resistance to styrene attack, easy degassing..
Tensile Strength, Yield	2.50 MPa	363 psi	50 mm/min
Arkema Group Evatane® 1350 VN 5 Ethylene Vinyl Acetate EVA copolymer made by high pressure tubular process. Applications Grade for molding very flexible articles. Examples: gaskets.ISO data provided by the manufacturer, Arkema.