Ascend Performance Materials Vydyne® R550H Nylon 66, 50% Glass Reinforced, DAM

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled
Manufacturer Ascend Performance Materials (formerly Solutia)
Trade Name VYDYNE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ascend Performance Materials Vydyne® R550H Nylon 66, 50% Glass Reinforced, DAM.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Vydyne® R550H is general-purpose, heat-stabilized, hydrolysis-resistant, 50% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved flow and offers superior surface appearance. Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents. Vydyne R550H is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposures to long term heat. Also, Vydyne R550H has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions. Typical Applications/End Uses: Vydyne R550H is successfully used in a wide range of injection-molding engineering applications. Typical parts include automotive clips, radiator end-tanks and parts of the air-conditioning and fuel distribution systems; electrical connectors, housings and bobbins; and industrial applications such as gears, bearing shells, covers and housings. Availability:Asia PacificEuropeNorth AmericaFiller/Reinforcement:Glass Fiber, 50% Filler by WeightAdditive:LubricantHeat Stabilizer Features:Good FlowGood Mold ReleaseHeat Stabilized High RigidityHigh Strength Lubricated Uses:Automotive Under the HoodGearsHousingsPower/Other ToolsAppearance: Natural ColorForms: PelletsProcessing Method: Injection MoldingInformation provided by Ascend Performance Materials.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ISO 1183
Water Absorption 0.50 %

@Time 86400 sec
 0.50 %

@Time 24.0 hour
 ISO 62
Moisture Absorption at Equilibrium 1.2 %
1.2 %
50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm

@Diameter 2.00 mm
 0.0040 in/in

@Diameter 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm

@Diameter 2.00 mm
 0.0090 in/in

@Diameter 0.0787 in
 ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 240 MPa
34800 psi
ISO 527-2
Elongation at Break 2.5 %
2.5 %
ISO 527-2
Tensile Modulus 16.8 GPa
2440 ksi
ISO 527-2
Flexural Strength 350 MPa
50800 psi
ISO 178
Flexural Modulus 16.0 GPa
2320 ksi
ISO 178
Poissons Ratio 0.40
0.40
ISO 527-2
Izod Impact, Notched (ISO) 16.0 kJ/m²

@Temperature -30.0 °C
 7.61 ft-lb/in²

@Temperature -22.0 °F
 ISO 180
17.0 kJ/m²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 ISO 180
Charpy Impact Unnotched 9.10 J/cm²

@Temperature -30.0 °C
 43.3 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
9.50 J/cm²

@Temperature 23.0 °C
 45.2 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eU
Charpy Impact, Notched 1.40 J/cm²

@Temperature -30.0 °C
 6.66 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 1.20 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 0.667 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 10.0 µm/m-°C

@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C
 5.56 µin/in-°F

@Thickness 0.0787 in,
Temperature 73.4 - 131 °F
 ISO 11359-2
Melting Point 260 °C
500 °F
ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Unannealed; ISO 75-2/A
UL RTI, Electrical 140 °C

@Thickness 0.750 mm
 284 °F

@Thickness 0.0295 in
 UL 746
140 °C

@Thickness 1.50 mm
 284 °F

@Thickness 0.0591 in
 UL 746
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 130 °C

@Thickness 0.750 mm
 266 °F

@Thickness 0.0295 in
 UL 746
130 °C

@Thickness 1.50 mm
 266 °F

@Thickness 0.0591 in
 UL 746
130 °C

@Thickness 3.00 mm
 266 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 140 °C

@Thickness 0.750 mm
 284 °F

@Thickness 0.0295 in
 UL 746
140 °C

@Thickness 1.50 mm
 284 °F

@Thickness 0.0591 in
 UL 746
140 °C

@Thickness 3.00 mm
 284 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Glow Wire Test 675 °C

@Thickness 0.750 mm
 1250 °F

@Thickness 0.0295 in
 Flammability Index; IEC 60695-2-12
675 °C

@Thickness 1.50 mm
 1250 °F

@Thickness 0.0591 in
 Flammability Index; IEC 60695-2-12
700 °C

@Thickness 0.750 mm
 1290 °F

@Thickness 0.0295 in
 Ignition Temperature; IEC 60695-2-13
700 °C

@Thickness 1.50 mm
 1290 °F

@Thickness 0.0591 in
 Ignition Temperature; IEC 60695-2-13
750 °C

@Thickness 3.00 mm
 1380 °F

@Thickness 0.118 in
 Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 3.00 mm
 1760 °F

@Thickness 0.118 in
 Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm

@Thickness 3.00 mm
 1.00e+12 ohm-cm

@Thickness 0.118 in
 IEC 60093
Dielectric Strength 20.0 kV/mm

@Thickness 1.00 mm
 508 kV/in

@Thickness 0.0394 in
 IEC 60243
Arc Resistance 120 - 179 sec

@Thickness 3.00 mm
 120 - 179 sec

@Thickness 0.118 in
 ASTM D495
Comparative Tracking Index 400 - 499 V

@Thickness 1.00 mm
 400 - 499 V

@Thickness 0.0394 in
 IEC 60112
Hot Wire Ignition, HWI 7.0 - 14 sec

@Thickness 0.750 mm
 7.0 - 14 sec

@Thickness 0.0295 in
 UL 746
7.0 - 14 sec

@Thickness 3.00 mm
 7.0 - 14 sec

@Thickness 0.118 in
 UL 746
15 - 29 sec

@Thickness 1.50 mm
 15 - 29 sec

@Thickness 0.0591 in
 UL 746
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
 UL 746
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 UL 746
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
 UL 746
High Voltage Arc-Tracking Rate, HVTR 10.1 - 25.4 mm/min
0.398 - 1.00 in/min
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 280 - 310 °C
536 - 590 °F
Middle Barrel Temperature 280 - 310 °C
536 - 590 °F
Front Barrel Temperature 280 - 310 °C
536 - 590 °F
Nozzle Temperature 280 - 310 °C
536 - 590 °F
Melt Temperature 285 - 305 °C
545 - 581 °F
Mold Temperature 65.0 - 95.0 °C
149 - 203 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Suggested Max Regrind 25 %