PolyOne Geon™ Vinyl Rigid Extrusion L0313 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L0313 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 84 | 84 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 46.7 MPa | 6770 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 89.7 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.96 GPa | 429 ksi | ASTM D790 |
| Izod Impact, Notched | 1.40 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.62 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| Dart Drop Total Energy | 24.0 J/cm @Temperature 23.0 °C |
0.0450 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| 25.4 J/cm @Temperature 23.0 °C |
0.0476 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 72.0 µm/m-°C | 40.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.1 °C @Thickness 3.18 mm |
106 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent | |
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 10341 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Handles | |
| Profiles |
Users viewing this material also viewed the following:
- North Wood Plastics Polypropylene with 20% Wood Fiber, Molding Grade
- SABIC Innovative Plastics LNP FARADEX KX98009 Acetal Copolymer (Europe-Africa-Middle East)
- DSM Biomedical PurSil® AL 5 Aliphatic Thermoplastic Silicone Polyether Urethane (discontinued **)
- STAR Thermoplastic Alloys & Rubbers StarGrip GP 45-1000 TPE
- Teknor Apex Flexalloy® 3500-55 Polyvinyl Chloride Elastomer
- Westlake EMAC® SP2202 21.5% Ethylene-Methyl Acrylate Copolymer
- Toyobo GLAMIDE® T-521 Nylon-6
- ChevronTexaco Delo® 100 Motor Oil, SAE 40
- Adamas Adalon® 305 PTFE, 15% Graphite
Copyright © lookpolymers.com All Rights Reserved