ExxonMobil Bicor™ 20MBT666 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 20MBT666 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Bicor 20MBT666 is a biaxially oriented transparent polypropylene film acrylic coated two sides. This film is specifically suitable for unprinted overwrapping, offering unique aspect and cost reduction advantage.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdHigh seal strengths even under low pressure sealingExcellent packaging machine performanceOutstanding optical propertiesNo seal compatibility between acrylic coating and coex filmWater based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierIn Lamination Lap SealableApplications: Box OverwrapTobacco Uses: Tobacco Overwrap Flexible Packaging Processing Method: Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.40 g/m²/day @Temperature 23.0 °C	0.0900 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	6.98 g/m²/day @Temperature 38.0 °C	0.450 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	1000 cc/m²/day @Temperature 23.0 °C	64.5 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	1010 cc/m²/day @Temperature 23.0 °C	65.0 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	20.1 microns	0.790 mil	ExxonMobil Method
Coating Weight	17.9 g/m²	11.2 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	175 %	175 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	60 %	60 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.00 GPa	290 ksi	MD; ExxonMobil Method
	3.80 GPa	551 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Both Sides; ExxonMobil Method
Seal Strength	200 g/25 mm @Pressure 0.00345 MPa, Temperature 100 °C	200 g/in @Pressure 0.500 psi, Temperature 212 °F	0.5 sec, Untreated Surface; ExxonMobl Method
Film Tensile Strength at Break, MD	160 MPa	23200 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	6.0 % @Temperature 135 °C, Time 432 sec	6.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	5.5 % @Temperature 135 °C, Time 432 sec	5.5 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.2 %	1.2 %	ExxonMobil Method
Gloss	85 %	85 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	90°F	36.3 psi, 0.2 sec
Yield	38700 in²/lb