RheTech Products E206-01 Linear Low Density Polyethylene, Black
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products E206-01 Linear Low Density Polyethylene, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Flexible componentsConsumer GoodsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.929 g/cc | 0.929 g/cc | 23/23°C; ASTM D792 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 230 °C |
35 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength at Break | 10.3 MPa | 1500 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 0.241 GPa | 35.0 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 22.6 J | 16.7 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 57.2 °C | 135 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.6 °C | 96.0 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 138 - 154 °C | 280 - 310 °F | |
| Middle Barrel Temperature | 143 - 166 °C | 290 - 330 °F | |
| Front Barrel Temperature | 154 - 171 °C | 310 - 340 °F | |
| Nozzle Temperature | 149 - 160 °C | 300 - 320 °F | |
| Mold Temperature | 15.6 - 26.7 °C | 60.0 - 80.0 °F | |
| Drying Temperature | 37.8 - 48.9 °C | 100 - 120 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 9.65 MPa | 400 - 1400 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 315 Ground Alumina
- Polimeri Europa Europrene® 1502 F Emulsion Styrene-Butadiene Rubber
- SABIC Innovative Plastics Lexan® BM5225X PC (Asia Pacific)
- PolyOne Geon™ Vinyl Flexible A6DE3 Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC Innovative Plastics LNP STAT-KON WEF42I PBT
- Solvay TECHNYL® A 118L V50 PA66, 50% glass fiber, Eh 0
- Teknor Apex Sinvicomp DBS 5906 Polyvinyl Chloride, Rigid
- EMS-Grivory Grivory® BRZ 247 W PA6
- AlphaGary AlphaSeal™ 240-6CY Blue 7002 Polyolefin Thermoplastic Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP DFL36G PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved